PA6

PA6 LNP™ KONDUIT™ PX09322 WH SABIC INNOVATIVE US

263

Unit Price:US$ 5,250 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
71MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:wear resistant｜high strength｜Filler: Mineral filler
Application Areas:Automotive components｜Electronic and electrical components
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	130 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.2mm	UL 94	V-0
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break,50.0mmSpan	ASTM D790	81.0 Mpa
Tensile modulus		ASTM D638	10400 Mpa
tensile strength	Break	ASTM D638	51.0 Mpa
elongation	Break	ASTM D638	0.80 %
Bending modulus	50.0mmSpan	ASTM D790	11000 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	80.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	210 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	182 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	3.7E-05 cm/cm/°C
thermal conductivity	--5	ASTM D790/ISO 178	1.5 W/m/K
	thermal conductivity	--6	ASTM D790/ISO 178	6.0 W/m/K
		thermal conductivity	--7	ISO 22007-2	0.86 W/m/K
		thermal conductivity	thermal conductivity	--8	ISO 22007-2	2.7 W/m/K

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	Internal Method	0.58 %
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.53 %
Water absorption rate	24hr,50%RH	ASTM D570	0.060 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		ASTM D257	8.1E+14 ohms
Compared to the anti leakage trace index	CTI	UL 746	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 LNP™ KONDUIT™ PX09322 WH SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet