PC LEXAN™ XHT2141 NA7D005T SABIC INNOVATIVE US
178
- Unit Price:US$ 4,989 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:73.9MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility
- Application Areas:Automotive sector
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 46 g/10 min | |
| Melt volume flow rate | ISO 1133 | 43.0 cm3/10min | |
| Shrinkage rate | 内部方法 | 0.60 - 0.90 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| ISO 62 | 0.23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2600 Mpa | |
| ISO 527-2/1 | 2600 Mpa | ||
| tensile strength | ASTM D638 | 70.0 Mpa | |
| ISO 527-2/50 | 70.0 Mpa | ||
| ASTM D638 | 60.0 Mpa | ||
| ISO 527-2/50 | 60.0 Mpa | ||
| elongation | ASTM D638 | 6.5 % | |
| ISO 527-2/50 | 6.5 % | ||
| ASTM D638 | 90 % | ||
| ISO 527-2/50 | 90 % | ||
| Flexural modulus | ASTM D790 | 2550 Mpa | |
| ISO 178 | 2450 Mpa | ||
| bending strength | ISO 178 | 100 Mpa | |
| ASTM D790 | 110 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 9.0 kJ/m² | |
| ISO 179/1eA | 12 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| ISO 179/1eU | 无断裂 | ||
| Suspended wall beam without notch impact strength | ISO 180/1U | 无断裂 | |
| ISO 180/1U | 无断裂 | ||
| Dart impact | ASTM D3763 | 68.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+17 ohms | |
| Volume resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| dielectric strength | ASTM D149 | 23 KV/mm | |
| Dissipation Factor | ASTM D150 | 3.0 | |
| ASTM D150 | 3.1 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Metallic haze | 内部方法 | 155 °C |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 125 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 270 to 330 °C | ||
| Temperature in the middle of the barrel | 280 to 340 °C | ||
| Temperature at the front of the material cylinder | 290 to 350 °C | ||
| Spray nozzle temperature | 285 to 345 °C | ||
| Processing (melt) temperature | 290 to 350 °C | ||
| Temperature | 85 to 130 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 90 rpm | ||
| Exhaust hole depth | 0.025 to 0.080 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 155 °C | |
| ISO 75-2/Bf | 155 °C | ||
| ASTM D648 | 145 °C | ||
| ISO 75-2/Af | 142 °C | ||
| vicat | ASTM D152510 | 161 °C | |
| ISO 306/B50 | 160 °C | ||
| ISO 306/B120 | 162 °C | ||
| ball-indentation hardness | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | ASTM E831 | 6.0E-5 cm/cm/°C | |
| ASTM E831 | 6.0E-5 cm/cm/°C | ||
| ISO 11359-2 | 6.0E-5 cm/cm/°C | ||
| thermal conductivity | ASTM C177 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 150 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 150 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.