PEI

PEI ULTEM™ 2110EPR 1000 SABIC INNOVATIVE US

201

Unit Price:US$ 17,245 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Low viscosity｜enhance｜Flame retardant
Application Areas:Bottle cap
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Reverse notch impact	3.20 mm	ASTM D256	400 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.9 mm	UL 94	5VA
UL flame retardant rating	UL flame retardant rating	0.41 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break, 100 mm Span	ASTM D790	199 Mpa
Bending modulus	100 mm Span	ASTM D790	5240 Mpa
elongation	Break	ASTM D638	6.0 %
tensile strength	Break	ASTM D638	115 Mpa
tensile strength	tensile strength	Yield	ASTM D638	114 Mpa
Tensile modulus		ASTM D638	4610 Mpa

injection	Test Condition	Test Method	Test Result
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the rear of the barrel			330 to 400 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
drying time			4.0 to 6.0 hr
drying temperature			150 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Elec		UL 746	170 °C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	207 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	11 g/10 min

Electrical performance	Test Method	Test Result
Hot wire ignition	UL 746	PLC 1
High voltage arc tracing rate	UL 746	PLC 2
High arc combustion index	UL 746	PLC 4
Compared to the anti leakage trace index	UL 746	PLC 4
Arc resistance	ASTM D495	PLC 6

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 2110EPR 1000 SABIC INNOVATIVE US

Material Description

Technical Data Sheet Compare

Technical Data Sheet