ABS

ABS Novodur® HH-106 BK10009 INEOS STYRO THAILAND

397

Unit Price:US$ 2,772 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
26MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:heat-resisting
Application Areas:Electronic field｜Automotive sector｜Automotive interior parts｜Application in the automotive field
Color:--
Grade:Heat resistant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179	100 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	190 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2	520 kg/cm
tensile strength	tensile strength	Break	ISO 527-2	390 kg/cm
elongation	Yield	ISO 527-2	3.0 %
elongation	elongation	Break	ISO 527-2	25 %
Tensile modulus		ISO 527-2	25000 kg/cm
bending strength		ISO 178	770 kg/cm
Bending modulus		ISO 178	24000 kg/cm
Rockwell hardness			110 R
Vicat softening temperature		ISO 306	103 °C
Ball Pressure Test		ISO 2039-1	102 Mpa
Tensile modulus		ASTM D638	2500 Mpa
Tensile modulus	Tensile modulus		ISO 527-2	2400 Mpa
tensile strength	Yield,23°C	ASTM D638	52.0 Mpa
tensile strength	tensile strength	Yield,23°C	ISO 527-2	51.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	3.0 %
elongation	Break	ASTM D638	3.0 %
Nominal tensile fracture strain	23°C	ISO 527-2	9.0 %
Bending modulus		ASTM D790	2400 Mpa
Bending modulus	Bending modulus		ISO 178	2400 Mpa
bending strength		ASTM D790	77.2 Mpa
bending strength	bending strength		ISO 178	72.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
thermal conductivity		DIN 52612	0.17 W/m/K
Maximum operating temperature			85 °C
Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	107 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	99.0 °C
Vicat softening temperature	--	ISO 306/A50	115 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	106 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate		ASTM D570	0.3 %
melt mass-flow rate	220°C/10.0kg	ASTM D1238	7.0 g/10min
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	7.00 cm3/10min
Shrinkage rate	MD	ASTM D955	0.55 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.40-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.25 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	1E+15 ohms·cm
Dielectric strength	1.50mm	IEC 60243-1	39 KV/mm
Compared to the anti leakage trace index		IEC 60112	V

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS Novodur® HH-106 BK10009 INEOS STYRO THAILAND

Material Description

Technical Data Sheet Compare

Technical Data Sheet