ABS

ABS STAREX® VE-0856U Samsung Cheil South Korea

246

Unit Price:US$ 3,078 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Flame retardant
Application Areas:Home appliance components｜TV casing｜Display frame｜LCD TV
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	23 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	3.0mm	UL 94	V-05VB5VA
	UL flame retardant rating	2.5mm	UL 94	V-0
		UL flame retardant rating	2.0mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--5	ISO 178	64.0 Mpa
bending strength	bending strength	--4	ASTM D790	56.0 Mpa
Bending modulus	--5	ISO 178	2100 Mpa
Bending modulus	Bending modulus	--4	ASTM D790	2000 Mpa
elongation	Break	ISO 527-2/50	6.0 %
elongation	elongation	Break3	ASTM D638	13 %
tensile strength	Break	ISO 527-2/50	28.0 Mpa
	tensile strength	Break3	ASTM D638	27.0 Mpa
		tensile strength	Yield	ISO 527-2/50	42.0 Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	39.0 Mpa
Tensile modulus	--3	ASTM D638	2000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature		ISO 306/B50	90.0 °C
Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	72.0 °C
	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	80.0 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	84.0 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD:3.20mm	ISO 2577	0.36-0.44 %
	Shrinkage rate	TD:3.20mm	ISO 2577	0.38-0.47 %
		Shrinkage rate	TD:3.20mm	ASTM D955	0.38-0.47 %
		Shrinkage rate	Shrinkage rate	MD:3.20mm	ASTM D955	0.36-0.44 %
melt mass-flow rate	200°C/5.0kg	ASTMD1238	3.6 g/10min

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	95
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS STAREX® VE-0856U Samsung Cheil South Korea

Material Description

Technical Data Sheet Compare

Technical Data Sheet