optical performance	Test Condition	Test Method	Test Result	Test Unit
turbidity	2540μm	ASTM D1003	1.0	%
transmissivity	2540μm	ASTM D1003	88.0	%
Refractive index		ASTM D542	1.586
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap		ASTM D1822	546	kJ/m²
Dart impact	23°C	ASTM D3029	169	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	62.1	J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Impact strength of cantilever beam gap	23°C	ASTM D4812	3200	J/m
	Impact strength of cantilever beam gap	23°C	ISO 180/1A	65	kJ/m²
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	23°C	ASTM D256	690	J/m
Charpy Notched Impact Strength	23°C	ISO 179/1eA	65	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	12	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.70mm	UL 94	HB
Radiation board grade	UL		YES
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation	Yield	ASTM D638	7.0	%
tensile strength	Break	ASTM D638	68.9	Mpa
tensile strength	tensile strength	Yield	ASTM D638	62.1	Mpa
elongation	Break	ASTM D638	130	%
Bending modulus	50.0mmSpan	ASTM D790	2340	Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	10.0	mg
bending strength	Yield,50.0mmSpan	ASTM D790	96.5	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str		UL 746	130	°C
RTI Imp		UL 746	130	°C
specific heat		ASTMC351	1260	J/kg/°C
thermal conductivity		ASTMC177	0.25	W/m/K
RTI Elec		UL 746	130	°C
Linear coefficient of thermal expansion	MD：-40to95°C	ASTME831	6.8E-05	cm/cm/°C
Vicat softening temperature		ASTM D15257	154	°C
Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	129	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	138	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Outdoor applicability		UL 746C	f2
Water absorption rate	Equilibrium,100°C	ASTM D570	0.58	%
	Water absorption rate	Equilibrium,23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	24hr	ASTM D570	0.15	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	18	g/10min
density		ASTM D792	1.19	g/cm³
Specific volume		ASTM D792	0.835	cm³/g
density		ASTM D792	1.20	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	60Hz	ASTM D150	3.17
Dielectric constant	Dielectric constant	50Hz	ASTM D150	3.17
Dielectric strength	3.20mm,inAir	ASTM D149	15	KV/mm
Volume resistivity		ASTM D257	>1.0E+17	ohms·cm
Hot wire ignition	HWI	UL 746	PLC 2
Dielectric constant	1MHz	ASTM D150	2.96
Dissipation factor	50Hz	ASTM D150	9E-04
	Dissipation factor	60Hz	ASTM D150	9E-04
	Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.010
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 1
High voltage arc tracing rate	HVTR	UL 746	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale	ASTM D785	118
Rockwell hardness	Rockwell hardness	M-Sale	ASTM D785	70

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.