PC Makrolon® 6717 COVESTRO GERMANY
206
- Unit Price:US$ 8,569 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜High temperature resistance
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 115 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 139 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 127 °C | |
| Glass Transition Temperature | ISO 11357-2 | 146 °C | |
| vicat | -- | ISO 306/B50 | 146 °C |
| -- | ISO 306/B120 | 147 °C | |
| ball-indentation hardness | 139°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : 23 到 55°C | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 横向 : 23 到 55°C | ISO 11359-2 | 7.0E-5 cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
| RTI Elec | 2.0 mm | UL 746 | 125 °C |
| RTI Imp | 2.0 mm | UL 746 | 115 °C |
| RTI | 2.0 mm | UL 746 | 125 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.586 | |
| transmissivity | 1000 µm | ISO 13468-2 | 87.0 % |
| 2000 µm | ISO 13468-2 | 86.0 % | |
| 3000 µm | ISO 13468-2 | 85.0 % | |
| 4000 µm | ISO 13468-2 | 84.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 2.0 mm | UL 94 | V-0 |
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| 1.5 mm | IEC 60695-2-12 | 960 °C | |
| 3.0 mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 0.75 mm | IEC 60695-2-13 | 875 °C |
| 1.5 mm | IEC 60695-2-13 | 900 °C | |
| 3.0 mm | IEC 60695-2-13 | 900 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 43 % | |
| Application of Flame from Small Burner | DIN 53438-1 | K1. F1 | |
| flash temperature | ASTM D1929 | 450 °C | |
| UL flame retardant rating | 1.50 mm | IEC 60695-11-5 | 2.0 min |
| 1.50 mm | IEC 60695-11-5 | 2.0 min | |
| 2.00 mm | IEC 60695-11-5 | 2.0 min | |
| 2.00 mm | IEC 60695-11-5 | 2.0 min | |
| 3.00 mm | IEC 60695-11-5 | 2.0 min | |
| 3.00 mm | IEC 60695-11-5 | 2.0 min | |
| auto-ignition temperature | ASTM D1929 | 510 °C | |
| Vertical Bunsen Burner Test | 1.00 mm14 | FAR 25.853(b) | passed |
| 1.00 mm15 | FAR 25.853(a) | passed | |
| 3.00 mm14 | FAR 25.853(b) | passed | |
| 3.00 mm15 | FAR 25.853(a) | passed | |
| burning rate | > 1.00 mm | ISO 3795 | passed |
| Smoke density | with flame, CO 17 | AITM 3.0005 | 200 ppm |
| with flame, Ds 4 min | ASTM E662 | < 200 | |
| with flame, HCL 17 | AITM 3.0005 | < 1.0 ppm | |
| with flame, HCN 17 | AITM 3.0005 | notdetectable ppm | |
| with flame, HF 17 | AITM 3.0005 | < 5.0 ppm | |
| with flame, NO-NO2 17 | AITM 3.0005 | < 5.0 ppm | |
| with flame, SO2-H2O 17 | AITM 3.0005 | < 20 ppm |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C, 完全断裂 | ISO 179/1eA | 14 kJ/m² |
| 23°C, 局部断裂 | ISO 179/1eA | 70 kJ/m² | |
| Impact strength of simply supported beam without notch | -60°C | ISO 179/1eU | 无断裂 |
| -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | -30°C, 完全断裂 | ISO 180/A | 15 kJ/m² |
| 23°C, 局部断裂 | ISO 180/A | 60 kJ/m² | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 65.0 J |
| 23°C | ISO 6603-2 | 60.0 J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 6400 N |
| 23°C | ISO 6603-2 | 5500 N |
| film | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water Vapor Transmission Rate | 23°C, 85% RH, 100 µm | ISO 15106-1 | 15 g/m²/24 hr |
| Carbon dioxide transmittance | 23°C, 25.4 µm | ISO 2556 | 16900 cm³/m²/bar/24 hr |
| gas transmission rate | Carbon Dioxide : 100.0 µm | ISO 2556 | 3800 cm³/m²/bar/24 hr |
| Nitrogen : 25.4 µm | ISO 2556 | 510 cm³/m²/bar/24 hr | |
| Nitrogen : 100.0 µm | ISO 2556 | 120 cm³/m²/bar/24 hr | |
| Oxygen : 25.4 µm | ISO 2556 | 2760 cm³/m²/bar/24 hr | |
| Oxygen : 100.0 µm | ISO 2556 | 650 cm³/m²/bar/24 hr |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Apparent density | ISO 60 | 0.66 g/cm³ | |
| melt mass-flow rate | 300°C/1.2 kg | ISO 1133 | 3.0 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 3.00 cm3/10min |
| shrinkage rate | 横向流量 | ISO 2577 | 0.60 - 0.80 % |
| 流量 | ISO 2577 | 0.60 - 0.80 % | |
| 横向流量 : 280°C, 2.00 mm4 | ISO 294-4 | 0.75 % | |
| 流量 : 2.00 mm4 | ISO 294-4 | 0.70 % | |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.30 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.12 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 1.0E+16 ohms | |
| volume resistivity | 23°C | IEC 60093 | 1.0E+16 ohms·cm |
| dielectric strength | 23°C, 1.00 mm | IEC 60243-1 | 34 KV/mm |
| relative permittivity | 23°C, 100 Hz | IEC 60250 | 3.10 |
| 23°C, 1 MHz | IEC 60250 | 3.00 | |
| Dissipation Factor | 23°C, 100 Hz | IEC 60250 | 1.0E-3 |
| 23°C, 1 MHz | IEC 60250 | 9.0E-3 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 3 |
| 解决方案 B | IEC 60112 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 °C | ||
| Drying time - Dry Air Dryer | 4.0 hr | ||
| Suggested maximum moisture content | < 0.020 % | ||
| Suggested injection volume | 30 to 70 % | ||
| Temperature at the rear of the barrel | 250 to 270 °C | ||
| Temperature in the middle of the barrel | 270 to 290 °C | ||
| Temperature at the front of the material cylinder | 285 to 305 °C | ||
| Spray nozzle temperature | 270 to 305 °C | ||
| Processing (melt) temperature | 280 to 320 °C | ||
| mold temperature | 70 to 110 °C | ||
| Back pressure | 10.0 to 20.0 Mpa | ||
| Exhaust hole depth | 0.025 to 0.075 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2400 Mpa |
| tensile strength | 屈服, 23°C | ISO 527-2/50 | 67.0 Mpa |
| 断裂, 23°C | ISO 527-2/50 | 65.0 Mpa | |
| Tensile strain | 屈服, 23°C | ISO 527-2/50 | 6.4 % |
| 断裂, 23°C | ISO 527-2/50 | 110 % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | > 50 % |
| flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| bending strength | 23°C | ISO 178 | 98.0 Mpa |
| 3.5% 应变, 23°C | ISO 178 | 75.0 Mpa | |
| 23°C | ISO 178 | 7.1 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.