thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	262 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	254 °C
melting temperature		ASTM D3418	260 °C

flammability	Test Condition	Test Method	Test Result
0.60 mm, All Colors	0.60 mm, 所有颜色		HB

Impact resistance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength		ISO 180	68 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	横向流量	内部方法	0.32 %
shrinkage rate	shrinkage rate	流量	内部方法	0.13 %
Water absorption rate	24 hr, 23°C	ASTM D570	0.37 %

Electrical performance	Test Condition	Test Method	Test Result
dielectric constant	1.00 GHz	ASTM D2520	4.15
dielectric constant	dielectric constant	2.40 GHz	ASTM D2520	4.15
Dissipation Factor	1.00 GHz	ASTM D2520	0.011
Dissipation Factor	Dissipation Factor	2.40 GHz	ASTM D2520	0.011

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
drying time			4.0 to 12 hr
Suggested maximum moisture content			0.090 %
Temperature at the rear of the barrel			250 °C
Temperature at the front of the material cylinder			280 °C
Processing (melt) temperature			285 to 305 °C
mold temperature			80 to 120 °C

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	18500 Mpa
tensile strength	屈服	ISO 527-2	245 Mpa
Tensile strain	断裂	ISO 527-2	2.3 %
flexural modulus		ISO 178	15900 Mpa
bending strength	3.5% 应变	ISO 178	379 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.