PA66

PA66 Durethan® AKV60XF 900116 LANXESS GERMANY

234

Unit Price:US$ 3,472 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
35MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:Fiber grade
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	70 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	60 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	75 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	650 °C
Extreme Oxygen Index		ISO 4589-2	25 %
BurningBehavior		ISO 3795	passed

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break,23°C	ISO 527-2/5	180 Mpa
Tensile strain	Break,23°C	ISO 527-2/5	4.0 %
Tensile modulus	23°C	ISO 527-2/1	9500 Mpa
Bending strain	23°C	ISO 178/A	4.5 %
Bending modulus	23°C	ISO 178/A	8400 Mpa
bending strength	3.5%Strain,23°C	ISO 178/A	255 Mpa
bending strength	bending strength	23°C4	ISO 178/A	260 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B120	>230 °C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	125 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	245 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	250 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.0 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	5.5 %
Shrinkage rate	MD:120°C,4hr,3.00mm3	ISO 2577	0.040 %
	Shrinkage rate	MD:290°C,3.00mm2	ISO 2577	0.35 %
		Shrinkage rate	TD:120°C,4hr,3.00mm3	ISO 2577	0.070 %
		Shrinkage rate	Shrinkage rate	TD:280°C,3.00mm2	ISO 2577	1.3 %
Apparent density		ISO 60	0.70 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength	23°C,1.00mm	IEC 60243-1	35 KV/mm
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	1E+15 ohms
Relative permittivity	23°C,100Hz	IEC 60250	4.00
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.60
Dissipation factor	23°C,100Hz	IEC 60250	8E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.016
Compared to the anti leakage trace index	SolutionA	IEC 60112	V

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut		ISO 1874	PA66.GHWR.14-090.GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.