thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火, 6.40 mm, 注塑	ASTM D648	230 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火, 6.40 mm, 注塑	ASTM D648	85.0 °C
melting temperature		ASTM D3418	260 °C
Linear coefficient of thermal expansion	流动	ASTM D696	7.0E-5 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40082mm	UL 94	V-0

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	23°C, 3.20 mm, 注塑，Flow	ASTM D955	0.90 - 1.6 %
Water absorption rate	24 hr, 23°C	ASTM D570	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity	23°C	ASTM D257	1.0E+14 ohms·cm
dielectric strength	23°C, 1.00 mm	ASTM D149	22 KV/mm
dielectric constant	23°C, 1 MHz	ASTM D150	3.00
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V

injection	Test Condition	Test Method	Test Result
drying temperature			80 to 100 °C
drying time			4.0 to 5.0 hr
Suggested maximum moisture content			0.10 %
Temperature at the rear of the barrel			255 to 270 °C
Temperature in the middle of the barrel			260 to 275 °C
Temperature at the front of the material cylinder			260 to 275 °C
Spray nozzle temperature			270 to 280 °C
Processing (melt) temperature			260 to 280 °C
mold temperature			60 to 90 °C
Back pressure			0.490 to 1.96 Mpa
screw speed			60 to 200 rpm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	78.5 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	28 %
flexural modulus	23°C, 6.40 mm, 注塑	ASTM D790	3330 Mpa
bending strength	23°C, 6.40 mm, 注塑	ASTM D790	113 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.