PC LNP™ STAT-KON™ EXL1162T WH SABIC INNOVATIVE US
122
- Unit Price:US$ 3,289 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:18MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Ductility at low temperature｜Short molding cycle
- Application Areas:Electronic and Electrical Applications｜Aerospace Applications｜lens
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | L-Sale | ISO 2039-2 | 89 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:23to80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| TD:-40to95°C | ASTME831 | 7.6E-05 cm/cm/°C | |
| TD:23to80°C | ISO 11359-2 | 7.6E-05 cm/cm/°C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI | UL 746 | 130 °C | |
| Heat Deflection Temperature | 1.8MPa,未Annealed,3.20mm | ASTM D648 | 122 °C |
| 1.8MPa,未Annealed,64.0mm跨距10 | ISO 75-2/Af | 117 °C | |
| vicat | -- | ASTMD152511 | 139 °C |
| -- | ISO 306/B120 | 140 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40to95°C | ASTME831 | 7.5E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8mm | IEC 60695-2-13 | 850 °C |
| 3.0mm | IEC 60695-2-13 | 850 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmissivity | 2540μm | ASTM D1003 | 82.0 % |
| haze | 2540μm | ASTM D1003 | 3.0 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 20 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 19.0 cm3/10min |
| shrinkage rate | MD:3.20mm | Internal Method | 0.40-0.80 % |
| TD:3.20mm | Internal Method | 0.40-0.80 % | |
| water absorption rate | Saturation,23°C | ISO 62 | 0.12 % |
| Equilibrium,23°C,50%RH | ISO 62 | 0.093 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| surface resistivity | ASTM D257 | >1.0E+15 ohms | |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile modulus | --3 | ASTM D638 | 2260 Mpa |
| -- | ISO 527-2/1 | 2340 Mpa | |
| tensile strength | Yield4 | ASTM D638 | 58.6 Mpa |
| Yield | ISO 527-2/50 | 57.8 Mpa | |
| Break4 | ASTM D638 | 57.1 Mpa | |
| Break | ISO 527-2/50 | 56.8 Mpa | |
| elongation | Yield4 | ASTM D638 | 5.7 % |
| Yield | ISO 527-2/50 | 5.4 % | |
| Break4 | ASTM D638 | 120 % | |
| Break | ISO 527-2/50 | 120 % | |
| flexural modulus | 50.0mmSpan5 | ASTM D790 | 2250 Mpa |
| --6 | ISO 178 | 2150 Mpa | |
| bending strength | --6,7 | ISO 178 | 89.5 Mpa |
| 屈服,50.0mmSpan5 | ASTM D790 | 94.8 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 74.9 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.