PA66

PA66 Zytel® 408L NC010 DUPONT JAPAN

353

Unit Price:US$ 4,857 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance
Application Areas:Industrial machinery｜Industrial applications｜Non specific food applications
Color:--
Grade:Special level

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	15 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	15 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
	UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	0.75mm	UL 94	HB
Burning rate	1.00mm	ISO 3795	<100 mm/min
Extreme Oxygen Index		ISO 4589-2	19 %
FMVSS flammability		FMVSS302	B

mechanical properties	Test Condition	Test Method	Test Result
Tensile creep modulus	1hr	ISO 899-1	-- Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	-- Mpa
Nominal tensile fracture strain		ISO 527-2	35 %
Tensile strain	Yield	ISO 527-2	6.0 %
tensile strength	Yield	ISO 527-2	61.0 Mpa
Tensile modulus		ISO 527-2	2200 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.3E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	1.3E-04 cm/cm/°C
Melting temperature		ISO 11357-3	263 °C
Vicat softening temperature		ISO 306/B50	210 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	66.0 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	155 °C

Physical properties	Test Condition	Test Method	Test Result
MediumDensity			0.950 g/cm³
Top out temperature			190 °C
SpecificHeatCapacity of Melt			2600 J/kg/°C
ThermalConductivityofMelt			0.16 W/m/K
density		ISO 1183	1.09 g/cm³
Shrinkage rate	TD	ISO 294-4	1.5 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.5 %
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	7.0 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	2.2 %

Electrical performance	Test Condition	Test Method	Test Result
Dielectric strength		IEC 60243-1	34 KV/mm
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Surface resistivity		IEC 60093	-- ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	1MHz	IEC 60250	0.020
Dissipation factor	Dissipation factor	100Hz	IEC 60250	0.020
Relative permittivity	1MHz	IEC 60250	2.90
Relative permittivity	Relative permittivity	100Hz	IEC 60250	3.20

film	Test Condition	Test Method	Test Result
Tensile strain	Yield，MD	ISO 527-3	6.0 %

Supplementary Information	Test Condition	Test Method	Test Result
EmissionofOrganicCompounds		VDA277	35.0 µgC/g
Odor		VDA270	4.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA66 Zytel® 408L NC010 DUPONT JAPAN

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet