Material Properties:High mobility｜Non enhanced｜Good appearance
Application Areas:engineering application ｜Electronic and electrical accessories
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa未退火	ISO 75-2/Bf	127 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.80MPa退火	ISO 75-2/Af	108 °C
vicat		ISO 306/B50	128 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7.2E-05 cm/cm/°C

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 0.85mm

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	1E+16 Ω.cm
Surface Resistivity		IEC 60093	1E+17 Ω.cm
dielectric strength		IEC 60243-1	45 KV/mm
dielectric strength	dielectric strength	相对漏电起痕指数	IEC 60112	175 V

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD2.0mm	ISO 294-4	0.65 %
shrinkage rate	shrinkage rate	TD2.0mm	ISO 294-4	0.65 %
Water absorption rate	(23°C,24hr)	ISO 62	0.70 %
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	0.20 %
melt mass-flow rate	260℃/5.0Kg	ISO 1133	27 cm3/10min

mechanical properties	Test Condition	Test Method	Test Result
Elongation at break	23°C	ISO 527-2	>50 %
Tensile modulus	23°C	ISO 527-2	2500 Mpa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	42 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	14 kJ/m²
tensile strength	23°C	ISO 527-2	62 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.