PA6

PA6 Durethan® BKV15H2.0 BK LANXESS GERMANY

380

Unit Price:US$ 3,602 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
28MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Glass fiber reinforced
Application Areas:Home appliance components｜Automotive Applications｜Electronic and electrical components
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	34 kJ/m²
	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	23 kJ/m²
		Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	310 J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	400 J/m
Charpy Notched Impact Strength	23°C	ISO 179	36 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179	25 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield4	ASTM D638	37.7 Mpa
bending strength	--6	ISO 178	58.0 Mpa
bending strength	bending strength	--5	ASTM D790	60.7 Mpa
Bending modulus	--6	ISO 178	1800 Mpa
Bending modulus	Bending modulus	--5	ASTM D790	2140 Mpa
elongation	Break	ISO 527-2/50	35 %
elongation	elongation	Break4	ASTM D638	30 %
tensile strength	Break	ISO 527-2/50	30.0 Mpa
tensile strength	tensile strength	Yield	ISO 527-2/50	40.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	186 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	82.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	203 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9.3E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	96.0 °C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	97.0 °C
Vicat softening temperature	--	ASTM D15257	217 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	104 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	13.0 cm3/10min
melt mass-flow rate	200°C/5.0kg	ASTM D1238	1.1 g/10min
density	23°C	ISO 1183	1.03 g/cm³
density	density	--3	ASTM D792	1.03 g/cm³

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	108

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.