Material Description
- Material Properties:Thermal stability｜Antistatic｜High mobility
- Application Areas:Automotive Applications｜Electrical applications
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 90.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9 | ISO 75-2/Ae | 88.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8 | ISO 75-2/Af | 89.0 °C | |
| vicat | -- | ASTM D152510 | 98.0 °C |
| -- | ISO 306/B50 | 102 °C | |
| -- | ISO 306/B120 | 105 °C | |
| ball-indentation hardness | 98°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 8.4E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 9.5E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 9.5E-5 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23°C, Total Energy | ASTM D3763 | 30.0 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 220°C/10.0 kg | ASTM D1238 | 6.3 g/10 min |
| 260°C/5.0 kg | ASTM D1238 | 11 g/10 min | |
| Melt volume flow rate | 220°C/10.0 kg | ISO 1133 | 6.00 cm3/10min |
| 260°C/5.0 kg | ISO 1133 | 10.0 cm3/10min | |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.80 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 % |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 85 to 95 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.040 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 230 to 250 °C | ||
| Temperature in the middle of the barrel | 235 to 255 °C | ||
| Temperature at the front of the material cylinder | 245 to 260 °C | ||
| Spray nozzle temperature | 235 to 255 °C | ||
| Processing (melt) temperature | 255 to 270 °C | ||
| mold temperature | 60 to 85 °C | ||
| Back pressure | 0.300 to 1.00 Mpa | ||
| screw speed | 30 to 80 rpm | ||
| Exhaust hole depth | 0.038 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 1970 Mpa |
| -- | ISO 527-2/1 | 2040 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 40.0 Mpa |
| 屈服 | ISO 527-2/5 | 43.0 Mpa | |
| 断裂3 | ASTM D638 | 33.0 Mpa | |
| 断裂 | ISO 527-2/5 | 35.0 Mpa | |
| elongation | 屈服3 | ASTM D638 | 3.6 % |
| 屈服 | ISO 527-2/5 | 3.3 % | |
| 断裂3 | ASTM D638 | 60 % | |
| 断裂 | ISO 527-2/5 | 19 % | |
| flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2170 Mpa |
| --5 | ISO 178 | 2060 Mpa | |
| bending strength | --5,6 | ISO 178 | 64.0 Mpa |
| 屈服, 50.0 mm 跨距4 | ASTM D790 | 68.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.