Material Properties:High mobility｜Flame retardant｜Easy to process
Application Areas:Electrical applications｜household electrical appliances｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	94.0 °C
vicat	--	ISO 306/B50	106 °C
vicat	vicat	--	ISO 306/B120	108 °C
Linear coefficient of thermal expansion	MD：23到55°C	ISO 11359-2	4.8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	5.9E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0
	UL flame retardant rating	2.0mm	UL 94	5VB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %
MeltViscosity	260°C	ISO 11443-A	360 Pa·s
Melt volume flow rate	260°C/5.0kg	ISO 1133	10.0 cm3/10min
shrinkage rate	TD:260°C,3.00mm	ISO 2577	0.40-0.50 %
shrinkage rate	shrinkage rate	MD:260°C,3.00mm	ISO 2577	0.40-0.50 %
Water absorption rate	饱和,23°C	ISO 62	0.50 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23°C	ISO 527-2/1	3950 Mpa
tensile strength	屈服,23°C	ISO 527-2/50	63.0 Mpa
tensile strength	tensile strength	断裂,23°C	ISO 527-2/50	50.0 Mpa
Tensile strain	屈服,23°C	ISO 527-2/50	4.0 %
Tensile strain	Tensile strain	断裂,23°C	ISO 527-2/50	19 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.