Material Properties:wear resistant｜currency
Application Areas:Household appliances｜Household appliances｜Automotive sector｜Fitness equipment｜Thin walled products
Color:--
Grade:Injection grade

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	23-55℃ Longitudinal	ISO 11359 part 1/2	120 µm/m-℃
melting temperature	DSC,10 K/min	ISO 3146 method C1b	166 °C
Heat Deflection Temperature	1.8MPa	ISO 75 part 1/2	80 °C
vicat	VST/B/50	ISO 306	140 °C

Basic performance	Test Condition	Test Method	Test Result
density		ISO 1183	1.42 g/cm
melt mass-flow rate	7cm	ISO 1133	9.94 g/10min

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23℃	ISO 179 1eU	9.0 J/cm
Charpy Notched Impact Strength	低温-30℃	ISO 179 1eA	0.4 J/cm
Impact strength of simply supported beam without notch	低温-30℃	ISO 179 1eU	8.50 J/cm
Charpy Notched Impact Strength	23℃	ISO 179 1eA	0.4 J/cm
Tensile creep modulus	1 hour	ISO 899 part 1	2400 Mpa
Tensile creep modulus	Tensile creep modulus	1000 hours	ISO 899 part 1	1200 Mpa
ball-indentation hardness	30秒数值	ISO 2039 part 1	135 Mpa
tensile strength	50mm/min，屈服	ISO 527 part 1/2	53 Mpa
Elongation at break	50mm/min	ISO 527 part 1/2	16 %
elongation	50mm/min	ISO 527 part 1/2	7.0 %
Tensile modulus	1mm/min	ISO 527 part 1/2	2850 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.