PPA Zytel® HTNFR52G30NH BL759A DUPONT SHENZHEN
229
- Unit Price:US$ 5,646 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:enhance｜Glass fiber reinforced｜Thermal stability｜Flame retardant｜High temperature resistance
- Application Areas:Electronic communication accessories｜Electronic communication accessories
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | 23℃ | 125 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | °C | 258to313 | |
| 8.0Mpa, Not annealed | °C | 165to230 | |
| 1.8MPa, Not annealed | °C | 247to292 | |
| 0.45MPa, annealing | °C | 296to320 | |
| 0.45MPa, Not annealed | °C | 275to308 | |
| RTI | °C | 119to150 | |
| Continuous use temperature | °C | 140to186 | |
| horizontal | mm/mm/°C | 68.6E-5-127.0E-5 | |
| 1.8MPa, annealing | °C | 283to300 | |
| horizontal | mm/mm/°C | 63.5E-5-177.8E-5 | |
| flow | mm/mm/°C | 195.6E-5-25.4E-5 | |
| 0.45MPa, Not annealed | °C | 273to312 | |
| RTI Imp | °C | 118to150 | |
| RTI Elec | °C | 140to150 | |
| flow | mm/mm/°C | 38.1E-5-50.8E-5 | |
| 1.8MPa, Not annealed | °C | 249to304 | |
| flow | mm/mm/°C | 185.4E-5-25.4E-5 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | % | 23to25 | |
| Burning wire flammability index | °C | 743to960 | |
| Hot filament ignition temperature | °C | 721to926 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 4.178to19.964 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | V | |
| V |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃,24hr | % | 0.30to0.51 | |
| Balance, 23 ℃, 50% RH | % | 0.21to1.2 | |
| Lateral flow: 23 ℃ | 横向, 23℃ | mm/mm | 119.4E-3-0.254 |
| 23℃,24hr | % | 0.12to0.30 | |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 48.3E-3-129.5E-3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Fracture, 23 ℃ | 162.76to199.31 MPa | ||
| Yield, 23 ℃ | % | 1.5to2.6 | |
| 12.62to270.34 MPa | |||
| Fracture, 23 ℃ | 108.28to262.76 MPa | ||
| shear strength | 23℃ | 88.28to107.59 MPa | |
| Yield, 23 ℃ | 102.76to362.76 MPa | ||
| Poisson's ratio | 23℃ | 0.41 | |
| compressive strength | 23℃ | 142.76to196.55 MPa | |
| Yield, 23 ℃ | % | 1.4to2.5 | |
| Fracture, 23 ℃ | % | 1.5to3.1 | |
| % | 1.0to2.5 | ||
| Tensile modulus | 摩擦系数 | 0.15to0.52 | |
| Yield, 23 ℃ | 68.97to250.34 MPa | ||
| Fracture, 23 ℃ | 131.72to400.0 MPa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.