POM HOSTAFORM® C9021TF5 CELANESE USA
182
- Unit Price:US$ 5,842 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:52MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:wear resistant｜currency
- Application Areas:Household appliances｜Household appliances｜Automotive sector｜Fitness equipment｜Thin walled products
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 注塑成型 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | 23-55℃ Longitudinal | ISO 11359 part 1/2 | 110 µm/m-℃ |
| melting temperature | DSC,10 K/min | ISO 3146 method C1b | 166 °C |
| Heat Deflection Temperature | 1.8MPa | ISO 75 part 1/2 | 100 °C |
| vicat | VST/B/50 | ISO 306 | 150 °C |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.42 g/cm | |
| Water absorption rate | 23℃and50%RH | ISO 62 | 0.2 % |
| 饱和23℃ | ISO 62 | 0.75 % | |
| melt mass-flow rate | 8.5cm | ISO 1133 | 12.07 g/10min |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1440 | |
| shrinkage rate | ASTM D955 | - % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 8.5 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | 1 MHz | IEC 60250 | 4.20 |
| 低频100 Hz | IEC 60250 | 4.20 | |
| dielectric strength | IEC 60243 part 1 | 35 KV/mm | |
| Dissipation Factor | IEC 60250 | 0.008 1 MHz | |
| 低频100 Hz | IEC 60250 | 0.0025 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | 30秒数值 | ISO 2039 part 1 | 140 Mpa |
| tensile strength | 50mm/min，屈服 | ISO 527 part 1/2 | 65 Mpa |
| Elongation at break | 50mm/min | ISO 527 part 1/2 | 20 % |
| elongation | 伸长率 | ISO 527 part 1/2 | 9.0 % |
| Tensile modulus | 1mm/min | ISO 527 part 1/2 | 2800 Mpa |
| flexural modulus | ISO 178 | 2700 Mpa | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179 1eU | 12.0 J/cm |
| Charpy Notched Impact Strength | 低温-30℃ | ISO 179 1eA | 0.6 J/cm |
| Impact strength of simply supported beam without notch | 低温-30℃ | ISO 179 1eU | 12 J/cm |
| Charpy Notched Impact Strength | 23℃ | ISO 179 1eA | 0.6 J/cm |
| Tensile creep modulus | 1 hour | ISO 899 part 1 | 2400 Mpa |
| 1000 hours | ISO 899 part 1 | 1200 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.