PES LNP™ THERMOCOMP™ JFL-4036 SABIC INNOVATIVE US

280

Unit Price:US$ 25,430 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature creep resistance｜Dimensional stability
Application Areas:Electronic field｜mechanical｜Bearing retainer
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C3	ISO 180/1U	24	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	360	J/m
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	9.40	J
Dart impact	Dart impact	--	ISO 6603-2	2.47	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Wear factor	Washer	ASTM D3702Modified	60.0	10^-10in^5-min/ft-lb-hr
Friction coefficient	Static	ASTM D3702Modified	0.36
Friction coefficient	Friction coefficient	Dynamic	ASTM D3702Modified	0.46
bending strength	--	ISO 178	138	Mpa
bending strength	bending strength	--	ASTM D790	179	Mpa
Bending modulus	--	ISO 178	10800	Mpa
Bending modulus	Bending modulus	--	ASTM D790	9930	Mpa
elongation	Break	ISO 527-2	1.5	%
elongation	elongation	Break	ASTM D638	1.9	%
tensile strength	Break	ISO 527-2	89.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	129	Mpa
Tensile modulus	--	ISO 527-2/1	9540	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	10200	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	3.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	2.3E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan4	ISO 75-2/Af	210	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	208	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.50	%
Water absorption rate	Water absorption rate	24hr,50%RH	ASTM D570	0.29	%
Shrinkage rate	MD:24hr	ISO 294-4	0.10-0.30	%
	Shrinkage rate	TD:24hr	ISO 294-4	0.30-0.60	%
		Shrinkage rate	TD:24hr	ASTM D955	0.30-0.60	%
		Shrinkage rate	Shrinkage rate	MD:24hr	ASTM D955	0.10-0.40	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PES LNP™ THERMOCOMP™ JFL-4036 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index