PBT/PC

PBT/PC VALOX™ 357U-1001 SABIC INNOVATIVE SHANGHAI

379

Unit Price:US$ 4,225 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
209.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:UV resistance
Application Areas:switch｜Shell｜Roller
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m
Dart impact	23°C7	ASTM D3029	43.4 J
Dart impact	Dart impact	23°C	ASTM D3029	43.4 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.46mm	UL 94	HB
	UL flame retardant rating	0.64mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	5VA
Extreme Oxygen Index		ASTM D2863	30 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ASTM D638	48.3 Mpa
tensile strength	tensile strength	Break	ASTM D638	48.3 Mpa
elongation	Break	ASTM D638	110 %
Bending modulus	50.0mmSpan	ASTM D790	2070 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	82.7 Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	82.7 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	138 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	98.9 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	9.2E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	1.2E-04 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI		UL 746	140 °C

Physical properties	Test Condition	Test Method	Test Result
Specific volume		ASTM D792	0.750 cm³/g
Melt Volume Flow Rate (MVR)	250°C/5.0kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	MD3	Internal Method	1.0-1.4 %
	Shrinkage rate	MD4	Internal Method	0.80-1.1 %
		Shrinkage rate	TD3	Internal Method	1.2-1.6 %
		Shrinkage rate	Shrinkage rate	TD4	Internal Method	0.90-1.3 %
Water absorption rate	24hr	ASTM D570	0.080 %
Outdoor applicability		UL 746C	f2

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		ASTM D257	>1.2E+16 ohms·cm
Dielectric strength	1.60mm,inOil	ASTM D149	25 KV/mm
	Dielectric strength	3.20mm,inAir	ASTM D149	19 KV/mm
	Dielectric strength	Dielectric strength	3.20mm,inOil	ASTM D149	19 KV/mm
Dielectric constant	100Hz	ASTM D150	3.20
Dielectric constant	Dielectric constant	1MHz	ASTM D150	3.20
Dissipation factor	100Hz	ASTM D150	3E-03
Dissipation factor	Dissipation factor	1MHz	ASTM D150	0.030
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI	UL 746	PLC 2
High arc combustion index	HAI	UL 746	PLC 3
High voltage arc tracing rate	HVTR	UL 746	PLC 3
Hot wire ignition	HWI	UL 746	PLC 2

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	117

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PBT/PC VALOX™ 357U-1001 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet