PC LEXAN™ 953A-116 SABIC INNOVATIVE NANSHA
205
- Unit Price:US$ 3,400 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:35MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜Flame retardant｜UV resistance
- Application Areas:Casters｜Household appliances
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | 速率B/50 | ASTM D1525 | 151 °C |
| Heat Deflection Temperature | 0.45MPa，6.4mm，未退火 | ASTM D648 | 137 °C |
| 1.82MPa，6.4mm，未退火 | ASTM D648 | 132 °C | |
| Linear coefficient of thermal expansion | -40°C至95°C，流动 | ASTME831 | 6.84E-05 1/°C |
| thermal conductivity | ASTMC177 | 0.19 W/m-°C | |
| Relative temperature index, Elec | UL 746B | 130 °C | |
| Relative temperature index, Mechw/impact | UL 746B | 120 °C | |
| Relative temperature index, Mechw/oimpact | UL 746B | 130 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| transmittance | 2.54mm | ASTM D1003 | 85 % |
| Haze ratio | 2.54mm | ASTM D1003 | 1 % |
| refractive index | ASTM D542 | 1.586 - |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL certification, 94V-2 flame rating | UL 94 | 1.47 mm | |
| UL certification, 94V-0 flame rating | UL 94 | 2.99 mm | |
| UV-light,waterexposure/immersion | UL 746C | F1 - |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 比重 | ASTM D792 | 1.21 - |
| Specific volume | ASTM D792 | 0.83 cm³/g | |
| density | 比重 | ASTM D792 | 1.217 g/cm³ |
| Water absorption rate | 24hr | ASTM D570 | 0.15 % |
| Equilibrium,23°C | ASTM D570 | 0.35 % | |
| Equilibrium,100°C | ASTM D570 | 0.58 % | |
| Mold shrinkage flow, 3.2mm | SABICMethod | 0.5-0.7 % | |
| melt mass-flow rate | 300°C/1.2kgf | ASTM D1238 | 7 g/10min |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | >1.E+17 ohm-cm | |
| Dielectric strength, in air, 3.2mm | ASTM D149 | 16.7 KV/mm | |
| Relative permittivity, 50/60Hz | ASTM D150 | 3.01 - | |
| Relative permittivity, 1MHz | ASTM D150 | 2.96 - | |
| Dissipation factor, 50/60Hz | ASTM D150 | 0.0009 - | |
| Dissipation factor, 1MHz | ASTM D150 | 0.01 - | |
| Arc resistance, Tungsten{PLC} | ASTM D495 | PLC_7 | |
| Hot wire ignition (HWI) | HWI){PLC} | UL 746A | |
| High Voltage Arc Traceability Rate (HVTR) | HVTR){PLC} | UL 746A | PLC 3 |
| HighAmpereArcIgn,surface{PLC} | UL 746A | PLC_2 | |
| Compared to the Leakage Traceability Index (CTI) | UL){PLC} | UL 746A | PLC_3 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Taber abraser | CS-17,1kg | ASTM D1044 | 10 mg/1000cy |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 326 cm-kgf/cm |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 65 cm-kgf/cm |
| S型 | ASTM D1822 | 535 cm-kgf/cm² | |
| Dart impact (D3029), 23 ℃ | ASTM D3029 | 1728 cm-kgf | |
| tensile strength | TypeI,50mm/min | ASTM D638 | 630 Kgf/cm2 |
| TypeI,50mm/min | ASTM D638 | 560 Kgf/cm2 | |
| Tensile strain | TypeI,50mm/min | ASTM D638 | 7 % |
| TypeI,50mm/min | ASTM D638 | 90 % | |
| bending strength | 1.3mm/min,50mmSpan | ASTM D790 | 920 Kgf/cm2 |
| flexural modulus | 1.3mm/min,50mmSpan | ASTM D790 | 22800 Kgf/cm2 |
| Rockwell hardness | M-Scale | ASTM D785 | 70 - |
| R-Scale | ASTM D785 | 118 - |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.