PC/PTFE LNP™ LUBRICOMP™ DL-4530-BK SABIC INNOVATIVE US
313
- Unit Price:US$ 9,355 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Thermal stability｜High temperature resistance
- Application Areas:Electronic and Electrical Applications｜Automotive components｜Engine parts
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 128 °C |
| 1.8MPa,未退火,64.0mm跨距 | ISO 75-2/Af | 131 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 29 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 140 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 30.6 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 34.1 J |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：24小时 | ASTM D955 | 0.80-0.90 % |
| TD:24小时 | ISO 294-4 | 0.88 % | |
| MD:24小时 | ISO 294-4 | 0.83 % | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.12 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2 | 5.5 % |
| elongation | 断裂 | ASTM D638 | 38 % |
| flexural modulus | ASTM D790 | 2190 Mpa | |
| ISO 178 | 2400 Mpa | ||
| bending strength | ASTM D790 | 80.3 Mpa | |
| ISO 178 | 84.1 Mpa | ||
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.18 |
| Static | ASTM D3702Modified | 0.070 | |
| Wear factor | Washer | ASTM D3702Modified | 60.0 10^-10in^5-min/ft-lb-hr |
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| ISO 527-2/1 | 2200 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 51.7 Mpa |
| 屈服 | ISO 527-2 | 53.0 Mpa | |
| 断裂 | ASTM D638 | 47.6 Mpa | |
| 断裂 | ISO 527-2 | 50.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.1 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.