PC SD POLYCA™ 301-4 SUMITOMO JAPAN
195
- Unit Price:US$ 3,937 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R 计秤 | ISO 2039-2 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火 | ISO 75-2/Af | 130 °C |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 7.0E-5 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.585 | |
| transmissivity | 2000 µm | ISO 13468 | 89.0 % |
| Haze ratio | 2000 µm | ISO 14782 | 0.40 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| 3.0 mm | UL 94 | HB | |
| 0.44 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-2 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 无断裂 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2 kg | ISO 1133 | 4.0 g/10 min |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 4.00 cm3/10min |
| shrinkage rate | 流动 | 内部方法 | 0.50 - 0.70 % |
| 横向流动 | 内部方法 | 0.50 - 0.70 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| volume resistivity | IEC 60093 | 3.0E+16 ohms·cm | |
| dielectric strength | 1.00 mm | IEC 60243-1 | 31 KV/mm |
| relative permittivity | 2.00 mm, 100 Hz | IEC 60250 | 3.00 |
| 2.00 mm, 1 MHz | IEC 60250 | 3.00 | |
| Dissipation Factor | 2.00 mm, 100 Hz | IEC 60250 | 1.0E-3 |
| 2.00 mm, 1 MHz | IEC 60250 | 0.090 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 125 °C | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature at the rear of the barrel | 280 to 300 °C | ||
| Temperature in the middle of the barrel | 290 to 310 °C | ||
| Temperature at the front of the material cylinder | 310 to 330 °C | ||
| Spray nozzle temperature | 310 to 330 °C | ||
| mold temperature | 70 to 100 °C | ||
| screw speed | 60 to 100 rpm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 110 % |
| flexural modulus | ISO 178 | 2300 Mpa | |
| bending strength | ISO 178 | 92.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.