ABS POLYLAC® PA-758 TAIWAN CHIMEI
1205
- Unit Price:US$ 2,340 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:610.65MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
- Material Comparison:ABS TR557 LG CHEM KOREA
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:transparent
- Application Areas:Household goods｜Home appliance components｜Automotive sector
- Color:--
- Grade:Transparent level
Material Certification
TDS
TDS
SVHC
Processing
Statement
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.08 g/cm³ | |
| ISO 1183 | 1.08 g/cm³ | ||
| melt mass-flow rate | ASTMD1238 | 3.0 g/10min | |
| Shrinkage rate | ISO 294-4 | 0.30-0.70 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 107 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 57.0 Mpa | |
| tensile strength | ISO 527-2/50 | 42.0 Mpa | |
| ISO 527-2/50 | 33.0 Mpa | ||
| ASTM D638 | 39.7 Mpa | ||
| elongation | ASTM D638 | 40 % | |
| ISO 527-2/50 | 40 % | ||
| Flexural modulus | ASTM D790 | 1900 Mpa | |
| ISO 178 | 1900 Mpa | ||
| bending strength | ASTM D790 | 53.9 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 7.0 kJ/m² | |
| ISO 179 | 14 kJ/m² | ||
| Impact strength of cantilever beam gap | ASTM D256 | 150 J/m | |
| ASTM D256 | 160 J/m | ||
| ISO 180/1A | 7.0 kJ/m² | ||
| ISO 180/1A | 14 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ISO 75-2/A | 97.0 °C | |
| vicat | ASTM D15256 | 105 °C | |
| ISO 306/A50 | 104 °C | ||
| ISO 306/B50 | 96.0 °C | ||
| ISO 11359-2 | 9E-05 cm/cm/°C | ||
| Hot deformation temperature (HDT) | ASTM D648 | 88.0 °C | |
| ISO 75-2/A | 77.0 °C | ||
| ASTM D648 | 99.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.