ABS

ABS POLYLAC® PA-758 TAIWAN CHIMEI

1302

Unit Price:US$ 2,221 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
723.65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS TR557 LG CHEM KOREA

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:transparent
Application Areas:Household goods｜Home appliance components｜Automotive sector
Color:--
Grade:Transparent level

Material Certification

SGS

RoHS

MSDS

SGS

TDS

MSDS

RoHS

SVHC

Processing

Statement

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	14 kJ/m²
Impact strength of cantilever beam gap	23°C,3.20mm	ASTM D256	150 J/m
	Impact strength of cantilever beam gap	23°C,6.40mm	ASTM D256	160 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	14 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength	--5	ISO 178	57.0 Mpa
tensile strength	Yield	ISO 527-2/50	42.0 Mpa
	tensile strength	Break	ISO 527-2/50	33.0 Mpa
	tensile strength	tensile strength	--3	ASTM D638	39.7 Mpa
elongation	Break3	ASTM D638	40 %
elongation	elongation	Break	ISO 527-2/50	40 %
Bending modulus	--4	ASTM D790	1900 Mpa
Bending modulus	Bending modulus	--5	ISO 178	1900 Mpa
bending strength	--4	ASTM D790	53.9 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	97.0 °C
Vicat softening temperature	--	ASTM D15256	105 °C
	Vicat softening temperature	--	ISO 306/A50	104 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	96.0 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	9E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	88.0 °C
	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	77.0 °C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ASTM D648	99.0 °C

Physical properties	Test Condition	Test Method	Test Result
density	--	ASTM D792	1.08 g/cm³
density	density	23°C	ISO 1183	1.08 g/cm³
melt mass-flow rate	200°C/5.0kg	ASTMD1238	3.0 g/10min
Shrinkage rate		ISO 294-4	0.30-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	107

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

ABS POLYLAC® PA-758 TAIWAN CHIMEI

Material Description

Material Certification

Technical Data Sheet Compare

Technical Data Sheet