impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C,TotalEnergy	ASTM D3763	69.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield,50.0mmSpan	ASTM D790	98.0	Mpa
Bending modulus	50.0mmSpan	ASTM D790	2670	Mpa
elongation	Break	ASTM D638	120	%
elongation	elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ASTM D638	61.0	Mpa
tensile strength	tensile strength	Yield	ASTM D638	60.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	6.3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	6E-05	cm/cm/°C
Vicat softening temperature		ASTM D15254	142	°C
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	136	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.