PC/ABS CYCOLOY™ XCY620S BK SABIC INNOVATIVE NANSHA
229
- Unit Price:US$ 2,910 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance|High mobility
- Application Areas:Electrical applications|Home appliance components
- Color:--
- Grade:--
Technical Data Sheet
thermal performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTM D648 | 128 °C |
0.45MPa,Unannealed,64.0mmSpan | ISO 75-2/Bf | 126 °C | |
1.8MPa,未退火,3.20mm | ASTM D648 | 108 °C | |
1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 106 °C | |
vicat | ASTM D15259 | 129 °C | |
ISO 306/B120 | 130 °C | ||
ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
100°C10 | IEC 60695-10-2 | Pass | |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
Impact resistance | Test Condition | Test Method | Test Result |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 40 kJ/m² |
23°C | ISO 180/1A | 55 kJ/m² | |
Dart impact | -30°C,TotalEnergy | ASTM D3763 | 65.0 J |
23°C,TotalEnergy | ASTM D3763 | 55.0 J | |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
23°C | ISO 179/1eA | 60 kJ/m² |
Electrical performance | Test Condition | Test Method | Test Result |
---|---|---|---|
Surface Resistivity | IEC 60093 | >1.0E+16 ohms | |
volume resistivity | IEC 60093 | >1.0E+16 ohms·cm | |
dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 39 KV/mm |
1.60mm,在油中 | IEC 60243-1 | 25 KV/mm | |
3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
Physical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 20.0 cm3/10min |
265°C/5.0kg | ISO 1133 | 25.0 cm3/10min | |
shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
TD:3.20mm | 内部方法 | 0.50-0.70 % | |
Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
饱和,23°C | ISO 62 | 0.40 % | |
平衡,23°C,50%RH | ISO 62 | 0.13 % |
mechanical properties | Test Condition | Test Method | Test Result |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 2200 Mpa | |
tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
断裂 | ISO 527-2/50 | 56.0 Mpa | |
Tensile strain | 屈服 | ISO 527-2/50 | 4.5 % |
断裂 | ISO 527-2/50 | 100 % | |
flexural modulus | 50.0mmSpan | ASTM D790 | 2300 Mpa |
ISO 178 | 2200 Mpa | ||
bending strength | ISO 178 | 82.0 Mpa | |
Yield,50.0mmSpan | ASTM D790 | 86.0 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.