PC Makrolon® XT5010 COVESTRO GERMANY
197
- Unit Price:US$ 3,781 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:20MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:high viscosity｜High temperature resistance
- Application Areas:Electronic and electrical components｜Automotive Applications
- Color:--
- Grade:Optical grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | -- | ISO 306/B50 | 112 °C |
| -- | ISO 306/B120 | 114 °C | |
| RTI Elec | 1.5mm | UL 746 | 80.0 °C |
| RTI Imp | 1.5mm | UL 746 | 80.0 °C |
| RTI Str | 1.5mm | UL 746 | 80.0 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 800 °C |
| 3.0mm | IEC 60695-2-13 | 850 °C | |
| UL flame retardant rating | 0.830mm | UL 94 | V-2 |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 960 °C |
| 1.5mm | IEC 60695-2-12 | 960 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 825 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C,完全断裂 | ISO 179/1eU | 220 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.21 g/cm³ |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 34.0 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2700 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 75.0 Mpa |
| 断裂,23°C | ISO 527-2/50 | 60.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 5.0 % |
| 断裂,23°C | ISO 527-2/50 | 90 % | |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >50 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.