PA6 Durethan®  BKV35Q 901510 ENVALIOR WUXI

265
  • Unit Price:US$ 2,970 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    56MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Filler: Glass fiber reinforced material｜35% filler by weight
  • Application Areas:--
  • Color:--
  • Grade:--

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U75 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U70 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU80 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU70 kJ/m²
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating1.6mmUL 94HB
UL flame retardant rating3.2mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12650 °C
Extreme Oxygen IndexISO 4589-223 %
BurningBehavior>1.00mmISO 3795passed
mechanical propertiesTest ConditionTest MethodTest Result
Tensile strainBreak,23°CISO 527-2/53.0 %
Tensile creep modulus1hrISO 899-1-- Mpa
tensile strengthBreak,23°CISO 527-2/5180 Mpa
Tensile modulus23°CISO 527-2/110700 Mpa
Tensile creep modulus1000hrISO 899-1-- Mpa
Bending modulus23°CISO 178/A10700 Mpa
bending strength3.5%StrainISO 178/A280 Mpa
bending strength23°CISO 178290 Mpa
bending strengthFlexuralStrainatFlexuralStrength5(23°C)4.0 %
thermal performanceTest ConditionTest MethodTest Result
Linear coefficient of thermal expansionTD：23to55°CISO 11359-28E-05 cm/cm/°C
Linear coefficient of thermal expansionMD：23to55°CISO 11359-22E-05 cm/cm/°C
Melting temperatureISO 11357-3222 °C
Vicat softening temperature--ISO 306/B120>200 °C
Vicat softening temperature--ISO 306/B50200 °C
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C150 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A205 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B215 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 621.9 %
Water absorption rateSaturation,23°CISO 626.5 %
Shrinkage rateMD:120°C,2hr,2.00mm3ISO 294-40.070 %
Shrinkage rateMD:280°C,2.00mm2ISO 294-40.23 %
Shrinkage rateTD:120°C,2hr,2.00mm3ISO 294-40.14 %
Shrinkage rateTD:280°C,2.00mm2ISO 294-40.70 %
Apparent densityISO 600.70 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivity23°CIEC 600931E+15 ohms·cm
Surface resistivityIEC 600931E+14 ohms
Dielectric strength23°C,1.00mmIEC 60243-140 KV/mm
Relative permittivity23°C,100HzIEC 602504.00
Relative permittivity23°C,1MHzIEC 602504.00
Dissipation factor23°C,100HzIEC 602507E-03
Dissipation factor23°C,1MHzIEC 602500.015
Compared to the anti leakage trace indexSolutionAIEC 60112 V
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1230 Mpa
filmTest ConditionTest MethodTest Result
Thin film puncture strength--7ISO 6603-21060 N
Thin film puncture strength--6ISO 6603-23.30 J
Thin film puncture strength--7ISO 6603-23.90 J
Thin film puncture strength--6ISO 6603-2945 N
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA6.GR.14-110.GF35
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.