Material Description

Material Properties:UV resistance｜Flame retardant
Application Areas:Lighting applications｜Home appliance components
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ASTM D4812	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ASTM D4812	无断裂
Dart impact	23°C, Total Energy	ASTM D3763	66.0 J
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	875 °C
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	1.0 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield3	ASTM D638	68.0 Mpa
Tensile modulus	--	ISO 527-2/1	2400 Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2500 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	106 Mpa
bending strength	bending strength	--5,6	ISO 178	103 Mpa
Bending modulus	--5	ISO 178	2500 Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2400 Mpa
tensile strength	Break	ISO 527-2/50	52.0 Mpa
	tensile strength	Break3	ASTM D638	52.0 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/50	67.0 Mpa
elongation	Break	ISO 527-2/50	23 %
	elongation	Break3	ASTM D638	51 %
		elongation	Yield	ISO 527-2/50	6.0 %
		elongation	elongation	Yield3	ASTM D638	6.0 %

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			265 to 290 °C
Temperature in the middle of the barrel			275 to 300 °C
Temperature at the front of the material cylinder			290 to 310 °C
Spray nozzle temperature			280 to 305 °C
Processing (melt) temperature			290 to 310 °C
Mold temperature			70 to 95 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	131 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Be	131 °C
RTI Elec		UL 746	125 °C
RTI Imp		UL 746	120 °C
RTI		UL 746	125 °C
Vicat softening temperature	--	ISO 306/B120	139 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	6.6E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.2E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.0E-5 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.6E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	120 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9	ISO 75-2/Ae	120 °C
Vicat softening temperature	--	ASTM D152510	136 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	137 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.11 %
Water absorption rate	Water absorption rate	Saturation, 23°C	ISO 62	0.14 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.60 - 0.80 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.55 - 0.75 %
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	5.00 cm3/10min
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	5.0 g/10 min

Electrical performance	Test Condition	Test Method	Test Result
Dielectric constant	1.10 GHz	ASTM ES7-83	2.79
Dissipation factor	1.10 GHz	ASTM ES7-83	5.8E-3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.