LCP SUMIKASUPER® E4008-BK SUMITOMO JAPAN
350
- Unit Price:US$ 9,484 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:96MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Aging resistance｜Low viscosity｜dimensional stability
- Application Areas:Automotive sector
- Color:--
- Grade:--
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 1.3 % | |
| 内部方法 | 0.10 % | ||
| Water absorption rate | ASTM D570 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 91 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 527-1 | 48 % | |
| Soldering Resistance | 内部方法 | 330 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 150 Mpa | |
| elongation | ASTM D638 | 5.0 % | |
| Flexural modulus | ASTM D790 | 12300 Mpa | |
| ASTM D790 | 6300 Mpa | ||
| bending strength | ASTM D790 | 139 Mpa | |
| ASTM D790 | 39.0 Mpa | ||
| shear strength | ASTM D732 | 52.0 Mpa | |
| Poisson's ratio | ASTM D785 | 0.49 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 520 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | ASTM D150 | 4.50 | |
| ASTM D150 | 3.90 | ||
| Dissipation Factor | ASTM D150 | 0.018 | |
| ASTM D150 | 0.034 | ||
| arc resistance | ASTM D495 | 130 sec | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 130 °C | ||
| drying time | 4.0 to 24 hr | ||
| Temperature at the rear of the barrel | 330 to 350 °C | ||
| Temperature in the middle of the barrel | 350 to 370 °C | ||
| Temperature at the front of the material cylinder | 370 to 390 °C | ||
| Spray nozzle temperature | 370 to 390 °C | ||
| Processing (melt) temperature | 380 °C | ||
| Temperature | 40 to 160 °C | ||
| Injection Pressure | 120 to 160 Mpa | ||
| injection speed | 中等偏快 | ||
| pressure holding | 40.0 to 60.0 Mpa | ||
| Back pressure | 1.00 to 5.00 Mpa | ||
| screw speed | 50 to 100 rpm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 313 °C | |
| 内部方法 | 1.4E-5 cm/cm/°C | ||
| 内部方法 | 6.2E-5 cm/cm/°C | ||
| thermal conductivity | JIS R2618 | 0.57 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.