PC WONDERLITE® PC-110 TAIWAN CHIMEI

1187

Unit Price:US$ 2,348 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
434.7MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
PC Makrolon® 2805 COVESTRO GERMANY

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Medium viscosity｜Weather resistance｜transparent
Application Areas:chip｜Casters｜container
Color:--
Grade:Injection grade

Material Certification

RoHS

MSDS

RoHS

TDS

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.20 g/cm³
density	density		ISO 1183	1.20 g/cm³
melt mass-flow rate		ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)		ISO 1133	10.0 cm3/10min
Shrinkage rate		ISO 294-4	0.50-0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ASTM D785	77

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-2
UL flame retardant rating	UL flame retardant rating		UL 94	V-2

Mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	61.6 Mpa
	tensile strength		ISO 527-2/50	65.0 Mpa
	tensile strength	tensile strength		ISO 527-2/50	75.0 Mpa
elongation		ASTM D638	110 %
Tensile strain		ISO 527-2/50	120 %
Flexural modulus		ASTM D790	2340 Mpa
Flexural modulus	Flexural modulus		ISO 178	2400 Mpa
bending strength		ASTM D790	89.8 Mpa
bending strength	bending strength		ISO 178	90.0 Mpa

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength		ISO 179	75 kJ/m²
Impact strength of cantilever beam gap		ASTM D256	850 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180/1A	75 kJ/m²

Thermal performance	Test Condition	Test Method	Test Result
		ISO 11359-2	6.0E-5to8.0E-5 cm/cm/°C
Hot deformation temperature (HDT)		ASTM D648	146 °C
	Hot deformation temperature (HDT)		ISO 75-2/A	128 °C
	Hot deformation temperature (HDT)	Hot deformation temperature (HDT)		ISO 75-2/A	143 °C
vicat		ASTM D15257	150 °C
	vicat		ISO 306/A50	150 °C
	vicat	vicat		ISO 306/B50	145 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.