PA6 Ultramid® 8233G BASF GERMANY

396

Unit Price:US$ 3,100 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
122.8MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability｜high strength｜Oil resistant
Application Areas:Helmet｜Automotive Applications｜Engine parts
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C	Internal Method	4.07	J
Impact strength of cantilever beam gap	23°C	ISO 180	10	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-40°C	ISO 180	8.5	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	15	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	88	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	110	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D256	150	J/m
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.60mm	UL 94	HB
	UL flame retardant rating	0.71mm	UL 94	HB
		UL flame retardant rating	1.5mm	UL 94	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	23°C	ASTM D790	297	Mpa
	bending strength	65°C	ASTM D790	160	Mpa
		bending strength	90°C	ASTM D790	140	Mpa
			bending strength	121°C	ASTM D790	112	Mpa
			bending strength	bending strength	23°C	ISO 178	260	Mpa
Tensile modulus	120°C	ISO 527-2	3550	Mpa
Tensile modulus	Tensile modulus	150°C	ISO 527-2	3440	Mpa
tensile strength	Break,-40°C	ASTM D638	283	Mpa
tensile strength	tensile strength	Break,23°C	ASTM D638	195	Mpa
Tensile modulus	-40°C	ISO 527-2	10500	Mpa
	Tensile modulus	23°C	ISO 527-2	10100	Mpa
	Tensile modulus	Tensile modulus	80°C	ISO 527-2	4430	Mpa
tensile strength	Break,80°C	ASTM D638	110	Mpa
	tensile strength	Break,121°C	ASTM D638	83.0	Mpa
		tensile strength	Break,-40°C	ISO 527-2	283	Mpa
		tensile strength	tensile strength	Break,23°C	ISO 527-2	185	Mpa
Bending modulus	-40°C	ASTM D790	9830	Mpa
elongation	Break,80°C	ASTM D638	7.0	%
elongation	elongation	Break,121°C	ASTM D638	7.0	%
Tensile strain	Break,-40°C	ISO 527-2	3.6	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2	3.5	%
tensile strength	Break,80°C	ISO 527-2	110	Mpa
	tensile strength	Break,120°C	ISO 527-2	83.0	Mpa
	tensile strength	tensile strength	Break,150°C	ISO 527-2	80.0	Mpa
elongation	Break,-40°C	ASTM D638	3.6	%
elongation	elongation	Break,23°C	ASTM D638	3.5	%
Tensile strain	Break,80°C	ISO 527-2	7.0	%
	Tensile strain	Break,120°C	ISO 527-2	7.0	%
	Tensile strain	Tensile strain	Break,150°C	ISO 527-2	6.0	%
Bending modulus	23°C	ASTM D790	9040	Mpa
	Bending modulus	65°C	ASTM D790	4020	Mpa
		Bending modulus	90°C	ASTM D790	3750	Mpa
			Bending modulus	121°C	ASTM D790	3320	Mpa
			Bending modulus	Bending modulus	23°C	ISO 178	8200	Mpa
bending strength	-40°C	ASTM D790	380	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
RTI Str	3.0mm	UL 746	140	°C
	RTI Str	1.5mm	UL 746	140	°C
	RTI Str	RTI Str	0.71mm	UL 746	130	°C
RTI Imp	3.0mm	UL 746	120	°C
RTI Elec	0.71mm	UL 746	130	°C
Linear coefficient of thermal expansion	TD		7E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD		2.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05	cm/cm/°C
Melting temperature		ISO 3146	220	°C
Melting temperature	Melting temperature		ASTM D3418	220	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	210	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
		Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	218	°C
RTI Imp	1.5mm	UL 746	115	°C
RTI Imp	RTI Imp	0.71mm	UL 746	115	°C
RTI Elec	3.0mm	UL 746	140	°C
RTI Elec	RTI Elec	1.5mm	UL 746	140	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792	1.39	g/cm³
density	density		ISO 1183	1.39	g/cm³
Shrinkage rate	MD：3.18mm		0.30	%
Water absorption rate	24hr	ASTM D570	1.1	%
	Water absorption rate	23°C,24hr	ISO 62	1.1	%
		Water absorption rate	Saturation	ASTM D570	6.4	%
			Water absorption rate	Saturation,23°C	ISO 62	6.4	%
				Water absorption rate	Equilibrium,50%RH	ASTM D570	1.8	%
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.8	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		IEC 60243-1	44	KV/mm
Volume resistivity		IEC 60093	>1.0E+13	ohms·cm
Volume resistivity	Volume resistivity	1.50mm	ASTM D257	>1.0E+13	ohms·cm
Dielectric constant	100Hz	IEC 60250	4.20
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.60
Dissipation factor	100Hz	IEC 60250	0.020
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.020
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PA6 Ultramid® 8233G BASF GERMANY

Material Description

Material Certification

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index