PA66 Leona™ FR370 ASAHI JAPAN
340
- Unit Price:US$ 4,490 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:108MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Halogen-free
- Application Areas:Laptop case｜switch｜Electrical components｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 85 |
| R计秤 | ASTM D785 | 120 | |
| M计秤 | ISO 2039-2 | 85 | |
| R计秤 | ISO 2039-2 | 120 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 难燃性 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat Deflection Temperature | HDT | ASTM D648/ISO 75 | 240 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 8 mm/mm.℃ | |
| Heat Deflection Temperature | 0.45MPa,未退火 | ASTM D648 | 240 °C |
| 0.45MPa,未退火 | ISO 75-2/B | 239 °C | |
| 1.8MPa,未退火 | ASTM D648 | 80.0 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 78.0 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.46MPa,干 | ASTM D-648 | 240 °C |
| 1.82MPa,干 | ASTM D-648 | 80 °C | |
| UL flame retardant rating | 干 | UL 94 | V-0 |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 7 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ASTM D2863 | 36 % |
| Basic performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 湿 | 2.3 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 58 kJ/m² |
| Other performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | 干 | ASTM D-2863 | 36 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257/IEC 60093 | 10*10 Ω.cm | |
| Surface Resistivity | ASTM D257 | 1E+13 ohms | |
| IEC 60093 | 1E+13 ohms | ||
| volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| 23°C | IEC 60093 | 1E+14 ohms·cm | |
| dielectric strength | ASTM D149 | 22 KV/mm | |
| IEC 60243-1 | 22 KV/mm | ||
| Compared to the Leakage Tracking Index (CTI) | 3.00mm | IEC 60112 | PLC 0 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.16 | |
| shrinkage rate | ASTM D955 | 0.9-1.6 % | |
| Water absorption rate | ASTM D570/ISO 62 | 2.3 % | |
| shrinkage rate | MD | 内部方法 | 0.90-1.6 % |
| Water absorption rate | 饱和,23°C | -- % | |
| 平衡,23°C,50%RH | ISO 62 | -- % | |
| shrinkage rate | 干 | 旭化成方法 | 0.9-1.6 % |
| Wear factor | 湿 | ASTM D-1044 | 7 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 29 kg·cm/cm(J/M)ft·lb/in | |
| Elongation at break | ASTM D638/ISO 527 | 7 % | |
| tensile strength | ASTM D638/ISO 527 | 83.4 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 3330 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 127 kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | 23°C | ISO 527-2 | 3600 Mpa |
| tensile strength | ASTM D638 | 83.0 Mpa | |
| 屈服,23°C | ISO 527-2 | 83.0 Mpa | |
| 断裂,23°C | ISO 527-2 | 80.0 Mpa | |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.5 % |
| elongation | 断裂 | ASTM D638 | 7.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 15 % |
| flexural modulus | ASTM D790 | 3300 Mpa | |
| 23°C | ISO 178 | 3600 Mpa | |
| bending strength | ASTM D790 | 128 Mpa | |
| 23°C | ISO 178 | 124 Mpa | |
| Taber abraser | 1000Cycles | ASTM D1044 | -- mg |
| tensile strength | 干(湿) | ASTM D-638 | 83(58) Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(110) R scale |
| Elongation at break | 干(湿) | ASTM D-638 | 7(70) % |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 29(58) J/m |
| bending strength | 干(湿) | ASTM D-790 | 128(56) Mpa |
| flexural coefficient | 干(湿) | ASTM D-790 | 3.3(1.3) GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 85(55) M Scale |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.