Material Properties:High rigidity｜Cold resistance｜heat-resisting｜Toughening｜ Used for extrusion molding｜Ultra high impact resistance｜High rigidity
Application Areas:Household appliances｜Helmet｜Electronic field｜Electrical field｜Extruded molded products｜Helmet｜Tubular products.
Color:--
Grade:Withdrawal level

Material Certification

MSDS

Processing

TDS

RoHS

SVHC

PSC

CSA

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	220℃×10kgf(98N)	ASTM D-1238(ISO 1133)	6.5	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength	23℃	ASTM D-638(ISO 527)	490(48)	kg/cm2(MPa)
bending strength	23℃	ASTM D-790(ISO 178)	740(73)	kg/cm2(MPa)
Bending modulus	23℃	ASTM D-790(ISO 178)	25000(2450)	kg/cm2(MPa)
Rockwell hardness	23℃	ASTM D-785(ISO 2039/2)	R-102
Impact strength of cantilever beam gap	23℃6.4mm	ASTM D-256(ISO R180)	46(451)	kg.cm/cm(J/m)
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	1Kg load	ASTM D-1525(ISO 306)	107	°C
Hot deformation temperature	Unanneaied 18.6kg/cm2(1/2"厚）	ASTM D-648(ISO 75/A)	92	°C
Hot deformation temperature	Hot deformation temperature	Annealed(8℃×8hr)	ASTM D-648(ISO 75/A)	104	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density	23℃/23℃	ASTM D-792(ISO 1183)	1.04

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.