PC LEXAN™ EXL1414 YW5G003NS SABIC INNOVATIVE NANSHA
148
- Unit Price:US$ 3,401 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:23MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Processability｜Moderate liquidity｜Ductility｜copolymer｜Good demolding performance
- Application Areas:Bottle cap｜Home appliance components｜Electrical applications
- Color:--
- Grade:Cold resistant grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | R计秤 | ASTM D785 | 121 |
| L计秤 | ASTM D785 | 89 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| vicat | ASTM D152510 | 145 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm | ASTM D648 | 124 °C |
| 1.8MPa,Unannealed,100mmSpan | ISO 75-2/Ae | 128 °C | |
| 0.45MPa,未退火,3.20mm | ASTM D648 | 139 °C | |
| 0.45MPa,Unannealed,100mmSpan | ISO 75-2/Be | 140 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| vicat | -- | ISO 306/B50 | 145 °C |
| -- | ISO 306/B120 | 146 °C | |
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 120 °C | |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C |
| TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7E-05 cm/cm/°C | |
| MD：23到80°C | ISO 11359-2 | 7.2E-05 cm/cm/°C | |
| RTI Str | UL 746 | 125 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 875 °C |
| 1.0mm | IEC 60695-2-13 | 875 °C | |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 850 °C | |
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 70.0 J |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 770 J/m |
| 23°C | ASTM D256 | 870 J/m | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 60 kJ/m² |
| 23°C | ISO 180/1A | 70 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | 1MHz | ASTM D150 | 9.3E-03 |
| 100Hz | ASTM D150 | 1.2E-03 | |
| dielectric constant | 1MHz | ASTM D150 | 2.64 |
| volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| dielectric strength | 0.800mm,inOil | ASTM D149 | 16 KV/mm |
| dielectric constant | 100Hz | ASTM D150 | 2.68 |
| Surface Resistivity | ASTM D257 | >1.0E+15 ohms |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| TD：3.20mm | 内部方法 | 0.40-0.80 % | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| density | ASTM D792 | 1.18 g/cm³ | |
| ISO 1183 | 1.19 g/cm³ |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 85.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 120 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2230 Mpa |
| ISO 178 | 2250 Mpa | ||
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| 断裂 | ASTM D638 | 50.3 Mpa | |
| 断裂 | ISO 527-2/50 | 60.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
| elongation | 断裂 | ASTM D638 | 98 % |
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 55.5 Mpa |
| Tensile modulus | ASTM D638 | 2020 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 92.4 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.