PC IUPILON™ GS2010MKR MITSUBISHI ENGINEERING JAPAN
153
- Unit Price:US$ 2,434 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High mobility｜Flame retardant｜enhance｜Filler: Glass fiber reinforced material｜10% filler by weight
- Application Areas:fibre
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 145 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 140 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.7E-05 cm/cm/°C | |
| ASTM D696/ISO 11359 | 4.0E-05 mm/mm.℃ |
| processability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dry conditions | 热风干燥 120℃---約4-8小时 | ||
| process temperature | 270-290 °C | ||
| 290-310 °C | |||
| 280-300 °C | |||
| screw speed | 50-100 rpm | ||
| mold temperature | 80-120 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 55 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10 g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 9.00 cm3/10min |
| shrinkage rate | TD:3.20mm | 0.40-0.60 % | |
| MD:3.20mm | 0.30-0.50 % | ||
| Water absorption rate | 饱和,23°C | ISO 62 | 0.14 % |
| density | ASTM D792/ISO 1183 | 1.27 | |
| shrinkage rate | ASTM D955 | 0.3 - 0.5 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 4500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 78.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.9 % |
| flexural modulus | ISO 178 | 4000 Mpa | |
| bending strength | ISO 178 | 135 Mpa | |
| Elongation at break | ASTM D638/ISO 527 | 3.4 % | |
| Tensile modulus | ASTM D638/ISO 527 | 4200 kg/cm²(MPa)[Lb/in²] | |
| flexural modulus | ASTM D790/ISO 178 | 3500 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 120 kg/cm²(MPa)[Lb/in²] |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App