Material Properties:Toughening｜transparent｜UV resistance｜High impact resistance｜Food contact compliance｜standard｜High transparency｜High Impact and GPPS Blending Extrusion｜Also suitable for injection molding｜Blow molding
Application Areas:Profile
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Basic performance	Test Method	Test Result
Water absorption rate	ISO 62	0.07 %
Melt volume flow rate	ISO 1133	11 CM
density	ISO 1183	1.01 g/cm
Water absorption rate	ISO 62	0.07 %

Mechanical properties	Test Method	Test Result
Impact strength of simply supported beam without notch	ISO 179/1eU	100/30 KJ/m
Shore hardness	ISO 868	D58
elongation at break	ISO 527-2	>50 %
Charpy Notched Impact Strength	ISO 179/1eA	4/3 KJ/m
elongation	ISO 527-2	2.3 %
Yang's modulus	ISO 527-2	1550 Mpa
tensile strength	ISO 527-2	28 Mpa

Electrical performance	Test Method	Test Result
dielectric strength	IEC 93	140 KV/mm
dielectric constant	IEC 250	2.5
Surface Resistivity	IEC 243/1	>10
Volume resistivity	IEC 93	>10 Ω.cm

Thermal performance	Test Method	Test Result
Heat distortion temperature	ISO 75	55 °C
UL	UL 94	HB/HB CLASS
Injection molding melting temperature		180-250 °C
vicat	ISO 306	59 °C
Injection mold temperature		30-50 °C
Extrusion molding melting temperature		190-230 °C
vicat	ISO 306	85 °C
Heat distortion temperature	ISO 75	75 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.