PA6

PA6 Akulon® K224-G9 DSM HOLAND

370

Unit Price:US$ 3,736 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75 kJ/m²

flammability	Test Condition	Test Method	Test Result
Hot filament ignition temperature	2.0mm	IEC 60695-2-13	725 °C
Hot filament ignition temperature	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	725 °C
Burning wire flammability index	2.0mm	IEC 60695-2-12	700 °C
Burning wire flammability index	Burning wire flammability index	1.5mm	IEC 60695-2-12	700 °C
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	0.75mm	IEC 60695-11-10,-20	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	9500 Mpa
tensile strength	Break	ISO 527-2	180 Mpa
Tensile strain	Break	ISO 527-2	3.5 %
Bending modulus		ISO 178	8600 Mpa
bending strength		ISO 178	235 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	220 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	MD	ISO 294-4	0.30 %
Water absorption rate	Saturation,23°C	ISO 62	6.3 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	1.9 %
Shrinkage rate	TD	ISO 294-4	0.90 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	100Hz	IEC 60250	3.50
Dielectric strength		IEC 60243-1	30 KV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Surface resistivity		IEC 60093	-- ohms
Compared to the anti leakage trace index		IEC 60112	V
Dissipation factor	1MHz	IEC 60250	0.015
Dissipation factor	Dissipation factor	100Hz	IEC 60250	5E-03
Relative permittivity	1MHz	IEC 60250	3.30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Akulon® K224-G9 DSM HOLAND

Material Description

Technical Data Sheet Compare

Technical Data Sheet