PA66

PA66 A 50H1 SOLVAY SHANGHAI

335

Unit Price:US$ 3,832 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Flame retardant grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	90 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.40 mm	UL 94	V-0
	UL flame retardant rating	0.8 mm	UL 94	V-0
		UL flame retardant rating	1.6 mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.2 mm	UL 94	V-0
Burning wire flammability index	0.8 mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	1.6 mm	IEC 60695-2-12	960 °C
	Burning wire flammability index	Burning wire flammability index	3.2 mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	960 °C
	Hot filament ignition temperature	0.8 mm	IEC 60695-2-13	960 °C
	Hot filament ignition temperature	Hot filament ignition temperature	1.6 mm	IEC 60695-2-13	775 °C
Extreme Oxygen Index		ISO 4589-2	33 %
European Railways Certifications	R22	EN 45545-2	HL3
European Railways Certifications	European Railways Certifications	R23	EN 45545-2	HL3

mechanical properties	Test Condition	Test Method	Test Result
bending strength	23°C	ISO 178	135 Mpa
bending strength	bending strength	23°C	ASTM D790	125 Mpa
Bending modulus	23°C	ISO 178	3700 Mpa
Bending modulus	Bending modulus	23°C	ASTM D790	3800 Mpa
Tensile strain	Break, 23°C	ISO 527-2	12 %
tensile strength	Break, 23°C	ISO 527-2/1A	80.0 Mpa
tensile strength	tensile strength	Yield, 23°C	ISO 527-2/1A	85.0 Mpa
Tensile modulus	23°C	ISO 527-2/1A	3800 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			80 °C
Suggested maximum moisture content			0.20 %
Temperature at the rear of the barrel			260 to 270 °C
Temperature in the middle of the barrel			265 to 275 °C
Temperature at the front of the material cylinder			265 to 275 °C
Mold temperature			60 to 80 °C

thermal performance	Test Condition	Test Method	Test Result
Melting temperature		ISO 11357-3	263 °C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	85.0 °C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	237 °C

Physical properties	Test Condition	Test Method	Test Result
Outdoor applicability		UL 746C	f1
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.7 %
Water absorption rate	Water absorption rate	24 hr, 23°C	ISO 62	0.88 %
Shrinkage rate	Flow	ISO 294-4	1.5 %
Shrinkage rate	Shrinkage rate	横向Flow	ISO 294-4	1.3 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0
Dissipation factor		IEC 60250	0.017
Relative permittivity		IEC 60250	3.50
Dielectric strength	2.00 mm	IEC 60243-1	21 KV/mm
Dielectric strength	Dielectric strength	0.800 mm	IEC 60243-1	33 KV/mm
Volume resistivity		IEC 60093	3.0E+15 ohms·cm
Surface resistivity		IEC 60093	3.0E+15 ohms

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.