PC LEXAN™ 223R-111 SABIC INNOVATIVE US
199
- Unit Price:US$ 2,876 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:71.4MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜UV resistance
- Application Areas:Automotive sector｜Electrical appliances｜Plastic bag｜Lighting applications｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 70 |
| R 级 | ASTM D785 | 118 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 137 °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 °C | |
| vicat | ASTM D15257 | 154 °C | |
| Linear coefficient of thermal expansion | -40 到 95°C，流动 | ASTM E831 | 6.8E-5 cm/cm/°C |
| specific heat | ASTM C351 | 1260 J/kg/°C | |
| thermal conductivity | ASTM C177 | 0.25 W/m/K | |
| RTI Elec | UL 746 | 100 °C | |
| RTI Imp | UL 746 | 100 °C | |
| RTI | UL 746 | 100 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ASTM D542 | 1.586 | |
| transmissivity | 2540 µm | ASTM D1003 | 88.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 1.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | V-2 |
| 6.0 mm | UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 12 kJ/m² |
| 23°C | ISO 179/1eA | 65 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
| -30°C5 | ISO 180/1U | 无断裂 | |
| 23°C5 | ISO 180/1U | 无断裂 | |
| Dart impact | 23°C | ASTM D3029 | 169 J |
| Impact strength of cantilever beam gap | ASTM D1822 | 546 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 18 g/10 min |
| shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Water absorption rate | 24 hr | ASTM D570 | 0.15 % |
| 平衡, 23°C | ASTM D570 | 0.35 % | |
| 平衡, 100°C | ASTM D570 | 0.58 % | |
| Outdoor applicability | UL 746C | f1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | ASTM D257 | > 1.0E+17 ohms·cm | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 15 KV/mm |
| dielectric constant | 60 Hz | ASTM D150 | 3.17 |
| 50 kHz | ASTM D150 | 3.17 | |
| 1 MHz | ASTM D150 | 2.96 | |
| Dissipation Factor | 50 Hz | ASTM D150 | 9.0E-4 |
| 60 Hz | ASTM D150 | 9.0E-4 | |
| 1 MHz | ASTM D150 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Hot wire ignition (HWI) | UL 746 | PLC 4 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 60 % | ||
| Temperature at the rear of the barrel | 260 to 280 °C | ||
| Temperature in the middle of the barrel | 270 to 295 °C | ||
| Temperature at the front of the material cylinder | 280 to 305 °C | ||
| Spray nozzle temperature | 275 to 300 °C | ||
| Processing (melt) temperature | 280 to 305 °C | ||
| mold temperature | 70 to 95 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 40 to 70 rpm | ||
| Exhaust hole depth | 0.025 to 0.076 mm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | 屈服 | ASTM D638 | 62.0 Mpa |
| 断裂 | ASTM D638 | 65.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 7.0 % |
| 断裂 | ASTM D638 | 110 % | |
| flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2340 Mpa |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 93.0 Mpa |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.