other	Test Condition	Test Method	Test Result	Test Unit
characteristic			日常杂项物品
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate			3.2	g/10min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
elongation			30	%
tensile strength			47	Mpa
Impact strength of cantilever beam gap			7	kj/mm
Bending modulus			2400	Mpa
bending strength			65	Mpa
Rockwell hardness			85	L
Elongation at Break		ASTM D638/ISO 527	4	%
tensile strength		ASTM D638/ISO 527	64(断裂)	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R-69
Bending modulus		ASTM D790/ISO 178	3450	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	104	kg/cm²(MPa)[Lb/in²]
Impact strength of cantilever beam gap		ASTM D256/ISO 179	10	kg·cm/cm(J/M)ft·lb/in
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	HDT		72	°C
Combustibility (rate)		UL 94	HB
Vicat softening temperature		ASTM D1525/ISO R306	85	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Ambiguity degree	2m/m		2.5	%
Total Light Transmittance	2m/m		91	%
density		ASTM D792/ISO 1183	1.09
Shrinkage rate		ASTM D955	0.3-0.7	%
Water absorption rate		ASTM D570/ISO 62	0.2	%
melt mass-flow rate		ASTM D1238/ISO 1133	2.0	g/10min

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.