'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
POM Delrin® 900P NC010 DUPONT NETHERLANDS
14
- Unit Price:US$ 5,450 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :Dongguan Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Transaction Guarantee:
Supplier Information
Dongguan Xinda Chemical Co., Ltd
+86 755 ********View
serv********View
+86 ********View
For more details, please contact the supplier!
Material Description
- Material Properties:lubrication｜wear resistant｜High rigidity｜high strength｜enhance｜High impact resistance｜High mobility
- Application Areas:Home appliance components｜Fiber grade｜Thin walled products
- Color:--
- Grade:--
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 | kJ/m² |
| -40°C | ISO 180/1A | 8.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 200 | kJ/m² |
| -30°C | ISO 179/1eU | 200 | kJ/m² | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.0 | kJ/m² |
| -30°C | ISO 179/1eA | 7.0 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00mm | ISO 3795 | 20 | mm/min |
| Atomization | F-value(refraction) | ISO 6452 | 95 | % |
| G-value(condensate) | ISO 6452 | 2E-04 | g | |
| UL flame retardant rating | 0.8mm | UL 94 | HB | |
| 1.5mm | UL 94 | HB | ||
| 0.8mm | IEC 60695-11-10,-20 | HB | ||
| 1.5mm | IEC 60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile creep modulus | 1000hr | ISO 899-1 | 1500 | Mpa |
| 1hr | ISO 899-1 | 2800 | Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 23 | % | |
| Friction coefficient | vs.Itself-Dynamic,1hr | ASTM D1894 | 0.25 | |
| Bending modulus | ISO 178 | 3000 | Mpa | |
| Tensile modulus | ISO 527-2 | 3300 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 71.0 | Mpa |
| Tensile strain | Yield | ISO 527-2 | 12 | % |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Effective thermal diffusivity coefficient | 8E-08 | m²/s | ||
| AnnealingTime-Optional | 30.0 | min/mm | ||
| AnnealingTemperature | 160 | °C | ||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 1.2E-04 | cm/cm/°C |
| MD | ISO 11359-2 | 1.2E-04 | cm/cm/°C | |
| MD：23to55°C | ASTME831 | 1E-04 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 178 | °C | |
| Vicat softening temperature | ISO 306/B50 | 160 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 94.0 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 162 | °C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| density | ISO 1183 | 1.42 | g/cm³ | |
| melt mass-flow rate | ISO 1133 | 25 | g/10min | |
| Melt Volume Flow Rate (MVR) | 190°C/2.16kg | ISO 1133 | 21.0 | cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.9 | % |
| MD | ISO 294-4 | 1.9 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO 62 | 1.4 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO 62 | 0.40 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | IEC 60093 | 1E+14 | ohms·cm | |
| Relative permittivity | 100Hz | IEC 60250 | 3.80 | |
| 1MHz | IEC 60250 | 3.80 | ||
| Surface resistivity | IEC 60093 | >1.0E+15 | ohms | |
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 120 | |
| M-Sale | ISO 2039-2 | 92 | ||
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| EmissionofOrganicCompounds | VDA277 | 4.30 | µgC/g | |
| Emission | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.