PA66 Ultramid® C3U BASF GERMANY

273

Unit Price:US$ 9,371 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:currency｜Flame retardant｜High impact resistance
Application Areas:Electrical components｜Electronic insulation｜currency
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
ball-indentation hardness		ISO 2039-1	100 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD		8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		9E-05 cm/cm/°C
RTI Elec	0.38mm	UL 746	110 °C
	RTI Elec	0.75mm	UL 746	120 °C
		RTI Elec	1.5mm	UL 746	120 °C
		RTI Elec	RTI Elec	3.0mm	UL 746	120 °C
RTI Imp	0.38mm	UL 746	65.0 °C
	RTI Imp	0.75mm	UL 746	105 °C
		RTI Imp	1.5mm	UL 746	105 °C
		RTI Imp	RTI Imp	3.0mm	UL 746	105 °C
Heat Deflection Temperature	0.45MPa,未退火	ASTM D648	224 °C
	Heat Deflection Temperature	1.8MPa,未退火	ASTM D648	91.0 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	70.0 °C
melting temperature		ASTM D3418	243 °C
melting temperature	melting temperature		ISO 3146	243 °C
Linear coefficient of thermal expansion	MD	ASTME831	4E-05 cm/cm/°C
RTI Str	0.38mm	UL 746	65.0 °C
	RTI Str	0.75mm	UL 746	115 °C
		RTI Str	1.5mm	UL 746	120 °C
		RTI Str	RTI Str	3.0mm	UL 746	120 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.38mm	UL 94	V-0
	UL flame retardant rating	0.75mm	UL 94	V-0
		UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-0

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179	9.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	80 kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTM D256	32 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	43 J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	4.5 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
density		ASTM D792	1.16 g/cm³
density	density		ISO 1183	1.16 g/cm³
Melt volume flow rate	275°C/5.0kg	ISO 1133	140 cm3/10min
shrinkage rate	MD：3.18mm		0.80 %
Water absorption rate	饱和	ASTM D570	8.5 %
	Water absorption rate	饱和,23°C	ISO 62	8.5 %
		Water absorption rate	平衡,50%RH	ASTM D570	2.9 %
		Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	2.9 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity	1.50mm	ASTM D257	1E+13 ohms·cm
volume resistivity	volume resistivity		IEC 60093	1E+13 ohms·cm
dielectric strength		IEC 60243-1	32 KV/mm
dielectric constant	1MHz	IEC 60250	3.60
Dissipation Factor	1MHz	IEC 60250	0.020
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	屈服,23°C	ISO 527-2	75.0 Mpa
elongation	屈服,23°C	ASTM D638	5.0 %
Tensile strain	屈服,23°C	ISO 527-2	4.0 %
elongation	断裂,23°C	ASTM D638	50 %
Nominal tensile fracture strain	23°C	ISO 527-2	6.0 %
flexural modulus	23°C	ASTM D790	3000 Mpa
flexural modulus	flexural modulus	23°C	ISO 178	3000 Mpa
Tensile modulus	23°C	ISO 527-2	3500 Mpa
tensile strength	屈服,23°C	ASTM D638	83.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.