PA66

PA66 R515H NT Q531 ASCEND USA

203

Unit Price:US$ 4,540 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Filler: Glass fiber reinforced material｜15% filler by weight
Application Areas:Engine parts｜Power/Other Tools｜Shell｜Parts under the hood of a car
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30°C	ISO 179	32 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	39 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	HB
	UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile strain	Break,23°C	ISO 527-2	3.0 %
Bending modulus	23°C	ISO 178	5900 Mpa
tensile strength	Break,23°C	ISO 527-2	120 Mpa
Tensile modulus	23°C	ISO 527-2	6600 Mpa
bending strength	23°C	ISO 178	170 Mpa
Poisson's ratio		ISO 527-2	0.40

thermal performance	Test Condition	Test Method	Test Result
RTI Elec	3.0mm	UL 746	120 °C
	RTI Elec	1.5mm	UL 746	120 °C
	RTI Elec	RTI Elec	0.75mm	UL 746	120 °C
Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO 11359-2	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO 11359-2	3E-05 cm/cm/°C
Melting temperature		ISO 11357-3	260 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	241 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	258 °C
RTI Str	3.0mm	UL 746	120 °C
	RTI Str	1.5mm	UL 746	120 °C
	RTI Str	RTI Str	0.75mm	UL 746	115 °C
RTI Imp	3.0mm	UL 746	105 °C
	RTI Imp	1.5mm	UL 746	85.0 °C
	RTI Imp	RTI Imp	0.75mm	UL 746	85.0 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.2 %
Water absorption rate	Water absorption rate	23°C,24hr	ISO 62	1.0 %
Shrinkage rate	MD:23°C,2.00mm	ISO 294-4	0.50 %
Shrinkage rate	Shrinkage rate	TD:23°C,2.00mm	ISO 294-4	1.0 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	3.00mm	IEC 60112	V
Arc resistance	3.00mm	ASTM D495	PLC 5
Dielectric strength	1.00mm	IEC 60243	24 KV/mm
Volume resistivity	0.750mm	IEC 60093	1E+13 ohms·cm
High arc combustion index	0.75mm	UL 746	PLC 0
	High arc combustion index	1.5mm	UL 746	PLC 0
	High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 0
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Hot wire ignition	0.75mm	UL 746	PLC 4
	Hot wire ignition	1.5mm	UL 746	PLC 4
	Hot wire ignition	Hot wire ignition	3.0mm	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.