Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NoBreak
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
NoBreak
flammability
Test Condition
Test Method
Test Result
UL flame retardant rating
1.5mm
UL 94
HB
Burning wire flammability index
IEC 60695-2-12
850 °C
Extreme Oxygen Index
ISO 4589-2
25 %
mechanical properties
Test Condition
Test Method
Test Result
bending strength
23°C
ISO 178
105 Mpa
Bending modulus
23°C
ISO 178
2400 Mpa
Nominal tensile fracture strain
23°C
ISO 527-2/50
>50 %
Tensile strain
Yield,23°C
ISO 527-2/50
6.8 %
tensile strength
Yield,23°C
ISO 527-2/50
70.0 Mpa
Tensile modulus
23°C
ISO 527-2/1
2400 Mpa
thermal performance
Test Condition
Test Method
Test Result
RTI Str
UL 746
140 °C
RTI Imp
UL 746
130 °C
RTI Elec
UL 746
140 °C
Linear coefficient of thermal expansion
TD：23to55°C
ISO 11359-2
6.5E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD：23to55°C
ISO 11359-2
6.5E-05 cm/cm/°C
Vicat softening temperature
ISO 306/B120
170 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
148 °C
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
160 °C
Physical properties
Test Condition
Test Method
Test Result
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
0.12 %
Water absorption rate
Saturation,23°C
ISO 62
0.30 %
Shrinkage rate
MD:2.00mm
ISO 294-4
0.80 %
Shrinkage rate
TD:2.00mm
ISO 294-4
0.80 %
Melt Volume Flow Rate (MVR)
330°C/2.16kg
ISO 1133
17.0 cm3/10min
melt mass-flow rate
330°C/2.16kg
ISO 1133
17 g/10min
density
23°C
ISO 1183
1.17 g/cm³
Electrical performance
Test Condition
Test Method
Test Result
Surface resistivity
IEC 60093
1E+16 ohms
Volume resistivity
23°C
IEC 60093
1E+17 ohms·cm
Dielectric strength
23°C,1.00mm
IEC 60243-1
35 KV/mm
Relative permittivity
23°C,100Hz
IEC 60250
3.00
Relative permittivity
23°C,1MHz
IEC 60250
2.90
Dissipation factor
23°C,100Hz
IEC 60250
1E-03
Dissipation factor
23°C,1MHz
IEC 60250
8E-03
Compared to the anti leakage trace index
SolutionA
IEC 60112
PLC 2
Compared to the anti leakage trace index
SolutionB
IEC 60112
PLC 4
hardness
Test Condition
Test Method
Test Result
Ball Pressure Test
ISO 2039-1
120 Mpa
Supplementary Information
Test Condition
Test Method
Test Result
Electrolytic corrosion
23°C
IEC 60426
A1
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)