PC LEXAN™  EXL1132T WH6 G099X SABIC INNOVATIVE NANSHA

185
  • Unit Price:US$ 3,183 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    23MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low temperature resistance｜Easy to process｜High mobility｜UV resistance
  • Application Areas:Household appliances｜Automotive sector｜Electronic field｜Electrical field
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
turbidity2540 μmASTM D10033.0 %
transmissivity2540 μmASTM D100382.0 %
impact performanceTest ConditionTest MethodTest Result
Charpy Notched Impact Strength-30°CISO 179/1eA45 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA65 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CISO 180/1U无断裂
Suspended wall beam without notch impact strength23°CISO 180/1U无断裂
Dart impact23°C, Total EnergyASTM D376374.0 J
flammabilityTest ConditionTest MethodTest Result
Hot filament ignition temperature3.0 mmIEC 60695-2-13850 °C
Hot filament ignition temperature0.8 mmIEC 60695-2-13850 °C
Burning wire flammability index3.0 mmIEC 60695-2-12960 °C
UL flame retardant rating1.5 mmUL 94HB
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--2ASTM D6382260 Mpa
Tensile modulus--ISO 527-2/12340 Mpa
tensile strengthYield3ASTM D63858.0 Mpa
tensile strengthYieldISO 527-2/5057.0 Mpa
tensile strengthBreak3ASTM D63857.0 Mpa
tensile strengthBreakISO 527-2/5056.0 Mpa
elongationYield3ASTM D6385.7 %
elongationYieldISO 527-2/505.4 %
elongationBreak3ASTM D638120 %
elongationBreakISO 527-2/50120 %
Bending modulus50.0 mm Span4ASTM D7902240 Mpa
Bending modulus--5ISO 1782140 Mpa
bending strength--5,6ISO 17889.0 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79094.0 Mpa
injectionTest ConditionTest MethodTest Result
Exhaust hole depth0.025 to 0.076 mm
Screw speed40 to 70 rpm
Back pressure0.300 to 0.700 Mpa
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Spray nozzle temperature290 to 310 °C
Temperature at the front of the material cylinder295 to 315 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the rear of the barrel270 to 295 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
drying time3.0 to 4.0 hr
drying temperature120 °C
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648121 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span9ISO 75-2/Af116 °C
Vicat softening temperature--ASTM D152510138 °C
Vicat softening temperature--ISO 306/B120139 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
Linear coefficient of thermal expansionFlow : -40 to 95°CASTM E8317.5E-5 cm/cm/°C
Linear coefficient of thermal expansionFlow : 23 to 80°CISO 11359-27.5E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 95°CASTM E8317.6E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : 23 to 80°CISO 11359-27.6E-5 cm/cm/°C
RTI ElecUL 746130 °C
RTIUL 746130 °C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate300°C/1.2 kgASTM D123820 g/10 min
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113319.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.80 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.80 %
Water absorption rateSaturation, 23°CISO 620.12 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.090 %
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityASTM D257> 1.0E+15 ohms·cm
Surface resistivityASTM D257> 1.0E+15 ohms
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessL -SaleISO 2039-289
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.