PBT Cristin® LW9330-BK851 DUPONT USA
221
- Unit Price:US$ 3,769 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Low warpage｜Glass fiber reinforced｜Filler: Glass fiber reinforced material｜30% by weight ratio)｜30% filler by weight｜Anti warping｜Good surface performance (glass fiber reinforced
- Application Areas:Electronic and electrical components｜Automotive Applications｜Industrial applications｜Industrial applications｜Box/Shell/Cover/Set｜Automotive Applications
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO 3146 | 220 ℃ | |
| Heat Deflection Temperature | 1.80 Mpa，未退火 | ISO 75A-1 | 185 ℃ |
| UL flame retardant rating | 0.750 mm | UL 94 | HB |
| 1.50 mm | UL 94 | HB | |
| 3.00 mm | UL 94 | HB | |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 185 °C |
| melting temperature | ISO 11357-3 | 225 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 28 mm/min |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.75mm | IEC 60695-11-10,-20 | HB | |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 9.0 kJ/m² |
| -30°C | ISO 179/1eA | 9.0 kJ/m² | |
| 23°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 kJ/m² |
| 23°C | ISO 179/1eU | 55 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 7.0 kJ/m² |
| 23°C | ISO 180/1A | 7.0 kJ/m² | |
| Suspended wall beam without notch impact strength | -40°C | ISO 180/1U | 45 kJ/m² |
| 23°C | ISO 180/1U | 45 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | Flow | ISO 294-4 | 0.30 % |
| density | ISO 1183 | 1.42 g/cm | |
| shrinkage rate | Across Flow | ISO 294-4 | 0.60 % |
| Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.25 % |
| density | ISO 1183 | 1.42 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 13 g/10min | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 10.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 0.60 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 1.0 % |
| MediumDensity | 1.27 g/cm³ | ||
| Ejection Temperature | 170 °C | ||
| SpecificHeatCapacity of Melt | 1790 J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-1 | 2.3 % |
| Tensile modulus | 23℃ | ISO 527-1 | 9800 MPa |
| flexural modulus | 23℃ | ISO 178 | 8400 MPa |
| Impact strength of simply supported beam without notch | 23 ℃, Type 1, Edgewise | ISO 179 | 55 KJ/m |
| Suspended wall beam without notch impact strength | -40 ℃, Type 1 | ISO 180 | 55 KJ/m |
| 23 ℃, Type 1 | ISO 180 | 65 KJ/m | |
| Impact strength of cantilever beam gap | -40 °C, Type 1, Notch A | ISO 180 | 7 KJ/m |
| 23 °C, Type 1, Notch A | ISO 180 | 7 KJ/m | |
| Tensile modulus | ISO 527-2 | 9800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 135 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
| flexural modulus | ISO 178 | 8400 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App