PC PANLITE® MN-3705M TEIJIN JAPAN
66
- Unit Price:US$ 2,350 /MT
- Packaging Specification:
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:UV resistance｜Flame retardant
- Application Areas:Lighting applications｜Electrical components｜Battery box
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa未退火 | ISO 75-2/Bf | 108 °C |
| 1.80MPa退火 | ISO 75-2/Af | 95 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |
| TD | ISO 11359-2 | 7E-05 cm/cm/°C |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 0.80mm | |
| UL -94 | V-0 3.00mm | ||
| GWIT | 2.00mm | IEC 60695-2-12 | 960 °C |
| Relative temperature of heating wire | 2.00mm | IEC 60695-2-13 | 825 °C |
| UL flame retardant rating | UL -94 | V-2 0.40mm |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 Ω.cm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD4.0mm | ISO 294-4 | 0.50-0.70 % |
| TD4.0mm | ISO 294-4 | 0.50-0.70 % | |
| Water absorption rate | (23°C,24hr) | ISO 62 | 0.22 % |
| melt mass-flow rate | 280℃/2.16Kg | ISO 1133 | 27.0 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 95 Mpa |
| flexural modulus | 23°C | ISO 178 | 2300 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 50 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NB kJ/m² |
| tensile strength | 屈服,23°C | ISO 527-2 | 60 Mpa |
| 23°C | ISO 527-2 | 50 Mpa | |
| Elongation at break | 屈服,23°C | ISO 527-2 | 7.0 % |
| 23°C | ISO 527-2 | 100 % | |
| Tensile modulus | 23°C | ISO 527-2 | 2450 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.